Abstract:Monodisperse metal nanoparticles (NPs) with high activity and selectivity are among the most important catalytic materials. However, the intrinsic process to obtain well-dispersed metal NPs with tunable high density (ranging from 1013 to 1016 m−2) and thermal stability is not yet well understood. Herein, the preparation of metal NPs with tunable areal density from layered double hydroxide (LDH) precursors in which the metal cations were pre-dispersed at an atomic scale was explored. Large quantities of mesopores induced by the Kirkendall effect were formed on the as-calcined layered double oxide (LDO) flakes. The O atoms bonded with Fe3+ cations were easy to be extracted at a temperature higher than 750 °C, which greatly increased the mobility of Fe. Consequently, coalescence of the reduced Fe atoms into large NPs enhanced the Kirkendall effect, leading to the formation of monodisperse embedded Fe NPs on the porous LDO flakes. The flake morphology of LDHs was well preserved, and the areal density of Fe NPs on the LDO flakes can be well controlled through adjusting the Fe content in the LDH precursor. With higher Fe loading, larger Fe NPs with higher areal density were available. When the areal density was increased from 0.039 to 0.55, and to 2.1 × 1015 m−2, the Fe NPs embedded on the LDO flakes exhibited good catalytic performance for the growth of entangled carbon nanotubes (CNTs), aligned CNTs, and double helical CNTs, respectively. This work provides not only new insights into the chemical evolution of monodisperse NPs from an atomic metal-dispersed precursor, but also a general route to obtain tunable NPs as heterogeneous catalysts for chemical and material production.

Porous carbon confined formation of monodisperse iron nanoparticle yolk toward versatile nanoreactors for metal extraction.

Nanoscale Zero-Valent Iron in Mesoporous Carbon (nzvi@c): Stable Nanoparticles for Metal Extraction and Catalysis

Fabrication and Application of Magnetic Nanoreactor with Multiple Ultrasmall Cores and Mesoporous Shell in Fenton-Like Oxidation

General And Facile Method To Fabricate Yolk-Like Structural Magnetic Nanocatalysts

Preparation Of Magnetically Recyclable Yolk/Shell Fexoy/Pdpt@Ceo2 Nanoreactors With Enhanced Catalytic Activity

One-pot Fabrication of Yolk-Shell Nanospheres with Ultra-Small Au Nanoparticles for Catalysis.

Dendritic porous yolk@ordered mesoporous shell structured heterogeneous nanocatalysts with enhanced stability

From Metal–Organic Frameworks to Single‐Atom Fe Implanted N‐doped Porous Carbons: Efficient Oxygen Reduction in Both Alkaline and Acidic Media

Plasmolysis-Inspired Nanoengineering of Functional Yolk-Shell Microspheres with Magnetic Core and Mesoporous Silica Shell

Superparamagnetic Ag@Fe3o4 Core-Shell Nanospheres: Fabrication, Characterization And Application As Reusable Nanocatalysts

Small-size and Well-Dispersed Fe Nanoparticles Embedded in Carbon Rods for Efficient Oxygen Reduction Reaction.

Porous carbon protected magnetite and silver hybrid nanoparticles: morphological control, recyclable catalysts, and multicolor cell imaging.

Nano-Fe⁰ encapsulated in microcarbon spheres: synthesis, characterization, and environmental applications

Yolk-Shell Fe3 O4 @Void@N-Carbon Nanostructures Based on One-Step Deposition of SiO2 and Resorcinol-3-Aminophenol-Formaldehyde (R-APF) Cocondensed Resin Dual Layers onto Fe3 O4 Nanoclusters

Carbon Nanocapsules As Nanoreactors for Controllable Synthesis of Encapsulated Iron and Iron Oxides: Magnetic Properties and Reversible Lithium Storage

In situ biosynthesis of ultrafine metal nanoparticles within a metal-organic framework for efficient heterogeneous catalysis

Phthalocyanine Precursors To Construct Atomically Dispersed Iron Electrocatalysts

Facile preparation of tiny gold nanoparticle loaded magnetic yolk–shell carbon nanoreactors for confined catalytic reactions

Design of mesoporous ZnCoSiOx hollow nanoreactors with specific spatial distribution of metal species for selective CO2 hydrogenation

Monodisperse Embedded Nanoparticles Derived from an Atomic Metal-Dispersed Precursor of Layered Double Hydroxide for Architectured Carbon Nanotube Formation

Controllable Synthesis of Mesoporous Carbon Nanospheres and Fe-N/Carbon Nanospheres As Efficient Oxygen Reduction Electrocatalysts