Abstract:A large piezoelectric constant (d33) of ∼480 pC/N was attained in new ternary (1-x-y)K0.5Na0.5Nb0.96Sb0.04O3-xBaSnO3-yBi0.5Na0.5ZrO3 ceramics by forming rhombohedral-orthorhombic-tetragonal (R-O-T) phase boundary using the variations of x and y, and such a phase boundary was successfully confirmed by the convergent beam electron diffraction (CBED) patterns. For (1-x)K0.5Na0.5Nb0.96Sb0.04O3-xBaSnO3, the orthorhombic (O) phase is well-maintained for 0 ≤ x ≤ 0.015, and both the R and T phases can be introduced to (0.99-y)K0.5Na0.5Nb0.96Sb0.04O3-0.01BaSnO3-yBi0.5Na0.5ZrO3 with y = 0.025-0.04 by simultaneously tailoring their compositions (x and y); then, R-O-T multiphases can be well-established. The CBED patterns strongly support the existence of R-O-T multiphases in the ceramics with y = 0.035. When the phase transitions endure from O to R-O-T, their piezoelectric activity endures a leapfrog development from ∼165 to ∼480 pC/N. In the region of the R-O-T phase boundary, a large d33 of ∼480 pC/N was attained in the ceramics with x = 0.01 and y = 0.035. In addition, the ceramics with x = 0.01 and y = 0.04 possess a high strain of ∼0.274% due to the multiphases coexistence. According to the variations of dielectric and ferroelectric properties, the enhancement in εr and Pr plays a part in the improved d33 except for the R-O-T phase boundary. We believe that the (K, Na)NbO3 ternary systems can be used to promote piezoelectric activity by forming new phase boundaries.

Superior Piezoelectric Properties in Potassium–Sodium Niobate Lead‐Free Ceramics

New K0.48Na0.52NbO3–Bi(Zn0.5Zr0.5)O3 Lead-Free Ceramics: Microstructure and Piezoelectricity

New Potassium-Sodium Niobate Ceramics with A Giant D(33)

Lead-Free Piezoelectrics Based on Potassium-Sodium Niobate with Giant D(33)

Giant Piezoelectricity in Potassium-Sodium Niobate Lead-Free Ceramics

Preparation and Characterization on Piezo-/Ferro-electric Properties Of(1-X)(knn+lt)+xbi Ceramics

New Potassium-Sodium Niobate Lead-Free Piezoceramic: Giant-D(33) Vs. Sintering Temperature

Phase transition characteristics and associated piezoelectricity of potassium-sodium niobate lead-free ceramics

Electrical Performance and Conduction Mechanism of Potassium Sodium Niobate-Based Lead-Free Piezoceramics Via Two-Step Sintering Route

High Piezoelectricity and Stable Output in Alkali-Niobate-Based Lead-Free Ferroelectric Ceramics

The structural origin of enhanced piezoelectric performance and stability in lead free ceramics

High piezoelectricity in (K,Na)(Nb,Sb)O3–(Bi,La,Na,Li)ZrO3 lead-free ceramics

A high temperature stable piezoelectric strain of KNN-based ceramics

Giant Piezoelectricity And High Curie Temperature In Nanostructured Alkali Niobate Lead-Free Piezoceramics Through Phase Coexistence

High mechanical quality factor and piezoelectricity in potassium sodium niobate ceramics

Nanodomains in KNN‐Based Lead‐Free Piezoelectric Ceramics: Origin of Strong Piezoelectric Properties

High Piezoelectric Properties and High TC in KNN-Based Lead-Free Ceramics Sintered in Reducing Atmosphere

Phase Structure, Microstructure, and Piezoelectric Properties of Potassium-Sodium Niobate-Based Lead-Free Ceramics Modified by Ca

Large D(33) In (K,Na)(Nb,Ta,Sb)O-3-(Bi,Na,K)Zro3 Lead-Free Ceramics

Composition Dependence of Phase Structure and Piezoelectric Properties in (0.98 − X )(K 0.4 Na 0.6 )nbo 3 –0.02cazro 3 – X Bi 0.5 Na 0.5 HfO 3 Ternary Ceramics

Identification of Phase Boundaries and Electrical Properties in Ternary Potassium-Sodium Niobate-Based Ceramics