Antibacterial porous sponge fabricated with capric acid-grafted chitosan and oxidized dextran as a novel hemostatic dressing
Xiaoyu Wang,Qifeng Dang,Chengsheng Liu,Guozhu Chang,Hao Song,Qing Xu,Yue Ma,Boyuan Li,Bonian Zhang,Dongsu Cha
DOI: https://doi.org/10.1016/j.carbpol.2021.118782
IF: 10.723
2022-02-01
Carbohydrate Polymers
Abstract:This work aims to fabricate multifunctional hemostatic sponges (C-ODs). Porous C-ODs were first constructed by using capric acid-modified chitosan (CSCA) and oxidized dextrans (ODs) with different oxidation degrees. Batches of experiments showed that (i) CSCA (33.39% of grafting degree), ODs, and C-ODs (100-200 μm in pore size) were synthesized, evidenced by FT-IR, <sup>1</sup>H NMR, elemental analysis, hydroxylamine hydrochloride titration, and SEM results; (ii) among C-ODs, C-OD<sub>2</sub> had appropriate porosity (85.0%), swelling (20 times its dry weight), absorption, water retention, water vapor transmission, and mechanical properties; (iii) C-OD<sub>2</sub> possessed low toxicity (relative cell viability > 86%), low hemolysis rate (0.65%), suitable tissue adhesion (4.74 kPa), and strong antibacterial efficacy (five strains); and (iv) C-OD<sub>2</sub>'s dynamic blood clotting was within 30 s. In three animal injury models, C-OD<sub>2</sub>'s hemostasis time and blood loss were fairly lower than commercial gelatin sponge. Totally, C-OD<sub>2</sub> might serve as an ideal hemostatic dressing.
polymer science,chemistry, organic, applied