Low-Cost, Efficient, and Durable H-2 Production by Photoelectrochemical Water Splitting with CuGa3Se5 Photocathodes

Christopher P. Muzzillo,W. Ellis Klein,Zhen Li,Alexander Daniel DeAngelis,Kimberly Horsley,Kai Zhu,Nicolas Gaillard

DOI: https://doi.org/10.1021/acsami.8b01447

IF: 9.5

2018-01-01

ACS Applied Materials & Interfaces

Abstract:Photoelectrochemical (PEC) water splitting is an elegant method of converting sunlight and water into H-2 fuel. To be commercially advantageous, PEC devices must become cheaper, more efficient, and much more durable. This work examines low-cost polycrystalline chalcopyrite films, which are successful as photovoltaic absorbers, for application as PEC absorbers. In particular, Cu-Ga-Se films with wide band gaps can be employed as top cell photocathodes in tandem devices as a realistic route to high efficiencies. In this report, we demonstrate that decreasing Cu/Ga composition from 0.66 to 0.31 in Cu-Ga-Se films increased the band gap from 1.67 to 1.86 eV and decreased saturated photocurrent density from 18 to 8 mA/cm(2) as measured by chopped-light current-voltage (CLIV) measurements in a 0.5 M sulfuric acid electrolyte. Buffer and catalyst surface treatments were not applied to the Cu-Ga-Se films, and they exhibited promising stability, evidenced by unchanged CLIV after 9 months of storage in air. Finally, films with Cu/Ga = 0.36 (approximately stoichiometric CuGa3Se5) and 1.86 eV band gaps had exceptional durability and continuously split water for 17 days (similar to 12 mA/cm 2 at -1 V vs RHE). This is equivalent to, similar to 17 200 C/cm(2), which is a world record for any polycrystalline PEC absorber. These results indicate that CuGa3Se5 films are prime candidates for cheaply achieving efficient and durable PEC water splitting.