Effects of hydrogen on the fracture toughness of X80 steel base metal and girth weld under strong cathodic current with in-situ hydrogen charging
Yunying Xing,Zhile Yang,Xingcheng Yao,Xiuyun Wang,Minxu Lu,Lei Zhang,Lijie Qiao
DOI: https://doi.org/10.1016/j.engfailanal.2022.106143
IF: 4
2022-05-01
Engineering Failure Analysis
Abstract:In this study, the effects of hydrogen on the fracture toughness and crack propagation of X80 steel base metal and girth weld were assessed. The crack tip opening displacement (CTOD) tests were conducted under in-situ strong cathodic current hydrogen charging in simulated soil solutions and compared to the ones in air. Fracture surfaces and cracks were observed using scanning electron microscopy (SEM) and electron back-scattering diffraction (EBSD). Under in-situ cathodic hydrogen charging conditions, pre-hydrogen charging did not substantially affect the test results of fracture toughness, and hydrogen could quickly achieve the crack tips and exert its effect on crack propagation. In hydrogen-containing environments, X80 steel base metal and girth welds both experienced a decline in fracture toughness. The reduction of the fracture toughness in the base metal increased with increasing current density, reaching 33.2% at a current density of 50 mA/cm2. In turn, that of the girth welds remained almost unchanged, exceeding 45% at the current densities of 10 and 50 mA/cm2, indicating that the girth weld was more susceptible to hydrogen. The difference in the effects of hydrogen on the fracture toughness of the base metal and the weld was attributed to specific microstructural features of both materials. Compared with the weld, the base metal exhibited more refined microstructure, the higher HAGB fraction and the larger grain boundary density, which was conducive to crack arrest performance in hydrogen-containing environments.
engineering, mechanical,materials science, characterization & testing