Abstract:Natural porous mineral supported (TiO2/diatomite) photocatalyst was prepared via a modified sol–gel method using titanium (IV) butoxide (TBOT) and diatomite. The effect of TBOT dosage on adsorption capacity and photocatalytic activity for Rhodamine B (RhB) solution was investigated. The morphology and elemental distribution were determined by scanning electron microscopy with attached energy-dispersive X-ray detector. The porous and crystalline structures were characterized using nitrogen adsorption–desorption and X-ray diffraction techniques, respectively. The prepared TiO2/diatomite hybrid catalyst has shown relatively even porous structure and dispersion of TiO2 over the surface. This suggests that the diatomite matrix prevented the agglomeration of TiO2 particles. Initially, the surface area and pore volume of the hybrid catalyst were increased by adding TBOT then decreased for dosages higher than 1.0ml. The crystalline size of TiO2 immobilized on diatomite matrix by sol–gel method was around 20nm. When the experiments were carried out in the absence of diatomite, this value was increased to 33.73nm. The use of diatomite also promoted an increase of the transformation temperature of the crystalline phase anatase to rutile for the TiO2. The as-prepared TiO2/diatomite composite exhibited high photocatalytic activity (96.0% for 0.5h UV-light irradiation) for the degradation of RhB from wastewater as a result of its unique porous structure and optimum TiO2 loading. In addition, it can be easily separated from suspension and possess a good durability. This hybrid material holds great promise in the engineering field for the environmental remediation.

The Different Paths and Potential Risks of Photo(-Electro)-catalytic Degradation for Rhodamine B in Water by Graphene/tio 2 Membrane

The different paths and potential risks of photo(-electro)-catalytic degradation for rhodamine B in water by graphene/TiO2 membrane

Degradation of Aqueous Rhodamine B by Plasma Generated along the Water Surface and Its Enhancement Using Nanocrystalline Fe-, Mn-, and Ce-doped TiO2 Films

Photodegradation of Rhodamine B in Water Assisted by Titania Films Prepared Through a Novel Procedure

Photocatalytic degradation of rhodamine B and methylene blue by electrochemically prepared nano titanium dioxide/reduced graphene oxide/poly (methyl methacrylate) nanocomposite

Photocatalytic Membrane Reactor for Degradation of Acid Red B Wastewater

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Photocatalyst-coated Carbon Microtube Electrodes: Preparation and Characterization of Their Properties and Photocatalytic Degradation of Methylene Blue.

Aminated graphene quantum dots/CdS nanobelts for enhanced photocatalytic degradation of RhB dye under visible light

The Improved Photoelectrocatalytic Degradation of Rhodamine B Driven by the Half-Rectified Square Wave

Titanium Dioxide–Reduced Graphene Oxide Composites for Photocatalytic Degradation of Dyes in Water

Application of nanostructured graphene oxide/titanium dioxide composites for photocatalytic degradation of rhodamine B and acid green 25 dyes

Visible-light Photocatalytic Degradation of Rhodamine B over MWCNTs-TiO2 Composite Device

Photoelectrocatalytic degradation of rhodamine B on TiO 2 photonic crystals

Photocatalytic degradation of Remazol Red B and Rhodamine B dyes using TiO2 nanomaterial: estimation of the effective operating parameters

Electric-Agitation-Enhanced Photodegradation of Rhodamine B over Planar Photoelectrocatalytic Devices Using A Tio2 Nanosized Layer

Synergetic Degradation Of Rhodamine B At A Porous Znwo4 Film Electrode By Combined Electro-Oxidation And Photocatalysis

Photocatalytic degradation of Rhodamine B over TiO2/g-C3N4 and immobilized TiO2/g-C3N4 on stainless steel wire gauze under UV and visible light: A detailed kinetic analysis and mechanism of degradation

2D/2D BiOBr/(001)-TiO2 heterojunction toward enhanced photocatalytic degradation activity of Rhodamine B

Photocatalytic degradation of rhodamine B by using a nanocomposite of cuprous oxide, three-dimensional reduced graphene oxide, and nanochitosan prepared via one-pot synthesis