Tunable Pore Size from Sub-Nanometer to a Few Nanometers in Large-Area Graphene Nanoporous Atomically Thin Membranes
Xiaobo Chen,Shengping Zhang,Dandan Hou,Hongwei Duan,Bing Deng,Zhiyang Zeng,Bingyao Liu,Luzhao Sun,Ruiyang Song,Jinlong Du,Peng Gao,Hailin Peng,Zhongfan Liu,Luda Wang
DOI: https://doi.org/10.1021/acsami.1c06243
2021-06-16
Abstract:Membranes are key components in chemical purification, biological separation, and water desalination. Traditional polymeric membranes are subjected to a ubiquitous trade-off between permeance and selectivity, which significantly hinders the separation performance. Nanoporous atomically thin membranes (NATMs), such as graphene NATMs, have the potential to break this trade-off. Owing to their uniqueness of two-dimensional structure and potential nanopore structure controllability, NATMs are expected to have outstanding selectivity through molecular sieving while achieving ultimate permeance at the same time. However, a drastic selectivity discrepancy exists between the proof-of-concept demonstrations and scalable separation applications in graphene membranes. In this paper, we offer a possible solution to narrow this discrepancy by tuning the pore density and pore size separately with two successive plasma treatments. We demonstrate that by narrowing the pore size distribution, the selectivity of graphene membranes can be greatly increased. Low-energy argon plasma is first applied to nucleate high density of defects in graphene. Controlled oxygen plasma is then utilized to selectively enlarge the defects into nanopores with desired sizes. This method is scalable, and the fabricated 1 cm<sup>2</sup> graphene NATMs with sub-nanometer pores can separate KCl and Allura Red with a selectivity of 104 and a permeance of 1.1 × 10<sup>–6</sup> m s<sup>–1</sup>. The pores in NATMs can be further tuned from gas-selective sub-nanometer pores to a few nanometer size. The fabricated NATMs show a selectivity of 35 between CO<sub>2</sub> and N<sub>2</sub>. With longer enlargement time, a selectivity of 21.2 between a lysozyme and bovine serum albumin can also be achieved with roughly four times higher permeance than that of a commercial dialysis membrane. This research offers a solution to realize NATMs of tunable pore size with a narrow pore size distribution for different separation processes from sub-nanometer in gas separation or desalination to a few nanometers in dialysis.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c06243?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c06243</a>.Illustration of the traditional NATM fabrication method, estimation of defect density using the obtained Raman data, estimation of defect density using AC-STEM images, simulation of oxygen plasma, SEM images of transferred graphene on the PCTE, discussion of nanopore merging, and discussion of defect size-influenced <i>I</i>(D)/<i>I</i>(G) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c06243/suppl_file/am1c06243_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology