Effect of Cobalt on CeO2 Nanorod Supported Pt Catalyst: Structure, Performance, Kinetics and Reaction Mechanism in CO Oxidation
Wenjia Song,Yanbo Deng,Zhiwen Lv,Min Su,Liang,Heng Zheng,Dajun Wang,Shaojun Yuan,Like Ouyang
DOI: https://doi.org/10.1016/j.ces.2024.120212
IF: 4.7
2024-01-01
Chemical Engineering Science
Abstract:Catalytic oxidation represents a highly efficient and extensively employed approach for the elimination of CO in exhaust gas. Rationally designing and preparing catalysts with exceptional activity and stability in the presence of H2O and SO2 at low temperatures represent crucial avenues for future advancements. In this work, a series of Pt catalysts supported on CeO2 nanorods incorporated with varying amounts of Cobalt (Co/CeO2 ratio ranging from 0 to 10 %) were prepared and evaluated for their catalytic activity in CO oxidation under both dry and wet conditions. The ultrahigh dispersion of Pt, outstanding redox properties, and abundant oxygen vacancies on the surface of Co-doped CeO2 nanorod supported Pt catalysts were revealed by XRD, TEM, Raman spectroscopy and H-2-TPR techniques. The catalytic activity for CO oxidation strongly depends on the Co content and reaction conditions. Among them, Pt/Co-CeO2-5 % exhibits the highest CO oxidation performance with a T-90 (the temperature to achieve 90 % conversion of CO) of 170 degrees C under dry conditions, which is significantly lower by 140 degrees C compared to T-90 of Pt/CeO2. Pt/Co-CeO2-1 % demonstrates superior CO oxidation performance with a T-90 of 195 degrees C under wet conditions, exhibiting a reduction in temperature by 65 degrees C compared to the T-90 of Pt/CeO2. Moreover, Pt/Co-CeO2 exhibits excellent resistance to SO2 compared to Pt/CeO2. Kinetic studies, in situ DRIFT analysis and isotopic experiments demonstrated direct participation of H2O in the reaction. On the catalysts with a low Co/Ce ratio (Co/Ce < 0.03), CO readily reacts with hydroxyl groups dissociated from H2O to form carboxyl intermediates, which subsequently undergo rapid decomposition into CO2, resulting in an enhanced reaction rate of CO oxidation at low temperature.