Abstract:By using chemical reduction-deposition method, a nickel-modified multi-walled carbon nanotube material, symbolized as y% Ni/MWCNT, was prepared. The H-2-TPD measurement showed that the modification of metallic nickel to the MWCNT could significantly enhance its capability of dissociatively adsorbing hydrogen. With the y% Ni/MWCNT as promoter, highly active y% Ni/MWCNT-promoted Cu-ZnO-Al2O3 catalysts, symbolized as Cu6Zn3Al1-x% (y% Ni/MWCNT), were prepared by co-precipitation method. It was experimentally found that appropriate incorporation of a minor amount of the y% Ni/MWCNT into the Cu6Zn3Al1 could significantly enhance the catalyst activity for methanol synthesis. Under the reaction conditions of 2.0 MPa, V(H-2) : V(CO) : V(CO2) : V(N-2) = 62 : 30 : 5 : 3, GHSV = 2700 ml, (STP) (.) h(-1) (.) (g-cat.)(-1), the observed CO-conversion over the Cu6Zn3Al1-12.5% (8% Ni/MWCNT) catalyst reached 34%, with the corresponding methanol-STY at 442 mg (.) h(-1) (.) (g-cat.)(-1), which was about 38% and 17% higher than those over the Cu6Zn3Al1 and Cu6Zn3Al1-12.5% MWCNT catalysts as contrast, respectively, at the respective optimal operation temperature, 513 K and 503 K. Characterization of the catalyst revealed that the pre-reduced Cu6Zn3Al1-12.5% (8% Ni/MWCNT) system could reversibly adsorb a considerably greater amount of hydrogen under atmospheric pressure at temperatures ranging from room temperature to similar to 573 K. This unique feature would be beneficial to generating microenvironments with relatively high stationary-state concentration of active hydrogen-adspecies on surface of the functioning catalyst, thus being favorable to increasing the rate of the CO hydrogenation reactions.

Tuning the Adsorption Energy of Methanol Molecules along Ni‐N‐Doped Carbon Phase Boundaries by the Mott–Schottky Effect for Gas‐Phase Methanol Dehydrogenation

Atomically Dispersed Ni-Based Anti-Coking Catalysts for Methanol Dehydrogenation in a Fixed-Bed Reactor

Study of Highly Active Cu-based Catalyst Promoted by Nickel-Modified Multi-Walled Carbon Nanotubes for Methanol Synthesis

MOF-derived N-doped Carbon Coated CoP/carbon Nanotube Pt-based Catalyst for Efficient Methanol Oxidation

Strengthening the Activity and CO Tolerance with Bi-Component PtNi/NbN-C Catalyst for Methanol Alkaline Electrooxidation

Tailoring the electronic structure of PtNi nanoalloy for boosting methanol electro-oxidation reaction

Performance Exploration of Ni-Doped MoS2 in CO2 Hydrogenation to Methanol

Modulating the Acidic Properties of Mesoporous Mox-Ni0.8Cu0.2O Nanowires for Enhanced Catalytic Performance Toward the Methanolysis of Ammonia Borane for Hydrogen Production.

Mechanism Studies Concerning Carbon Deposition Effect of CO Methanation on Ni-based Catalyst Through DFT and TPSR Methods

S,N dual-doped carbon nanotubes as substrate to enhance the methanol oxidation performance of NiO nanoparticles

Spatial decoupling of dehydrogenation and CO oxidation by Ni-Co-Ti hierarchical trimetallic catalyst for electrocatalytic oxidation of methanol

Theoretical Investigation of Methanol Oxidation on Pt and PtNi Catalysts

Precision tuning of highly efficient Pt-based ternary alloys on nitrogen-doped multi-wall carbon nanotubes for methanol oxidation reaction

Phosphorus-doping-tuned PtNi concave nanocubes with high-index facets for enhanced methanol oxidation reaction

Multi-dimensional Pt/Ni(OH)2/nitrogen-doped Graphene Nanocomposites with Low Platinum Content for Methanol Oxidation Reaction with Highly Catalytic Performance

TiN@nitrogen-doped Carbon Supported Pt Nanoparticles As High-Performance Anode Catalyst for Methanol Electrooxidation

Pt-Decorate MOFs Derived Ni-N-C Materials as an Efficient Electrocatalyst for Methanol Oxidation

Metal organic frameworks‐derived NiO/NiCo2O4 heterostructures for effective methanol oxidation reaction

Tuning reverse water gas shift and methanation reactions during CO2 reduction on Ni catalysts via surface modification by MoOx

Composition-Tuned Pt-Skinned PtNi- Bimetallic Clusters As: Highly Efficient Methanol Dehydrogenation Catalysts

Synergistic Catalysis of PtM Alloys and Nickel Hydroxide on Highly Enhanced Electrocatalytic Activity and Durability for Methanol Oxidation Reaction