An Optical Dynamic Study of Mapbbr(3) Single Crystals Passivated with Mapbcl(3)/I-3-Mapbbr(3) Heterojunctions

Haizhou Lu,Huotian Zhang,Sijian Yuan,Jiao Wang,Yiqiang Zhan,Lirong Zheng

DOI: https://doi.org/10.1039/c6cp07182a

IF: 3.3

2017-01-01

Physical Chemistry Chemical Physics

Abstract:Recently, perovskite based solar cells have attracted lots of research interest, some of which is in the passivation of perovskite surfaces, particularly the heterojunction based surface passivation. In this study, the optical dynamics of MAPbBr(3) single crystals with and without heterojunction passivation were studied systematically by means of a time- resolved spectroscopic technique for the first time. The emission lifetime of MAPbBr(3) single crystals under two-photon (1064 nm) excitation is a few orders of magnitude longer than that measured under one-photon (355 nm or 532 nm) excitation. Interestingly, with surface passivation, the lifetime measured at 355 nm excitations could be tuned significantly, whereas the lifetime change under 1064 nm excitations was considerably less. Our results give a direct evidence of surface quench by comparing the lifetimes before and after surface passivation. Furthermore, the results demonstrate that proper MAPbCl(3)-MAPbBr(3) heterojunctions can dramatically reduce the recombination channels in the surface region, which can be potentially useful for perovskite based solar cells, light emitting diodes (LED), and sensitive detectors.