Abstract:Pt hollow nanospheres with a particle diameter of 110 nm and a shell thickness of about 5 nm were synthesized in bulk using selenium colloids with a particle diameter of 100 nm as a template. Transmission electron microscopy (TEM), high resolution transmission electron microscopy (HR-TEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy dispersive X-ray spectrocopy (EDX), and scanning electron microscopy (SEM) were used to determine their morphologies and structures. The electrocatalytic activity of the Pt hollow nanospheres modifying glassy carbon electrode toward methanol oxidation was measured by using methanol as the probe molecule. We show that the multiporous Pt hollow nanospheres composited of atomic clusters have a uniform particle size, good dispersity, a stable structure, a big surface area and good mass transfer performance. Cyclic voltammetry (CV) showed that when the current density of methanol oxidation was 0.10 mA.cm(-2) and upon positive scanning the methanol oxidation potential of the Pt hollow nanospheres was around 110 and 64 mV negative than that of the Pt solid nanoparticles and Pt black, respectively. Upon negative scanning the former species was about 51 and 13 mV negative than that of the latter two species, respectively. After 800 segments cyclic voltammetry scanning, upon positive scanning the peak current density of methanol oxidation on the Pt hollow nanospheres was found to be 13 and 15 times as high as that of the Pt solid nanoparticles and Pt black, respectively. Upon negative scanning the former species was about 19 and 38 times as high as that of the two latter species. Our experimental results show that the Pt hollow nanospheres have good electrocatalytic activity and stability toward methanol oxidation.

Synthesis of Hollow Platinum-Palladium Nanospheres with a Dendritic Shell As Efficient Electrocatalysts for Methanol Oxidation.

Hollow PtPd Nanorods with Mesoporous Shells As an Efficient Electrocatalyst for the Methanol-Oxidation Reaction.

Trimetallic PtPdCo Mesoporous Nanopolyhedra with Hollow Cavities

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Facile Synthesis of Ternary PtPdCu Alloy Hexapods As Highly Efficient Electrocatalysts for Methanol Oxidation

Tuning Surface Structure of Pd3Pb/PtnPb Nanocrystals for Boosting the Methanol Oxidation Reaction

PtPdRh Mesoporous Nanospheres: an Efficient Catalyst for Methanol Electro-Oxidation

Enhanced Oxygen Reduction and Methanol Oxidation Electrocatalysis over Bifunctional PtPdIr Mesoporous Hollow Nanospheres

Three-dimensional Palladium-Rhodium Nanosheet Assemblies: Highly Efficient Catalysts for Methanol Electrooxidation.

Preparation of High Catalytic Platinum Hollow Nanospheres and Their Electrocatalytic Performance for Methanol Oxidation

Synthesis of Hierarchical Platinum-Palladium-Copper Nanodendrites for Efficient Methanol Oxidation

Stepwise synthesis of "Pt-on-PdAg" hybrid trigonal/hexagonal nanocrystals for efficient electroxidation of methanol: Interface engineering for trimetallic electrocatalyst

Well-dispersed Platinum Nanoparticles Supported on Hierarchical Nitrogen-Doped Porous Hollow Carbon Spheres with Enhanced Activity and Stability for Methanol Electrooxidation

Smart design of hollow AuPt nanospheres with a porous shell as superior electrocatalysts for ethylene glycol oxidation

Synthesis And Characterization Of Sub-10 Nm Platinum Hollow Spheres As Electrocatalyst Of Direct Methanol Fuel Cell

Facile Synthesis of Hollow Dendritic Ag/Pt Alloy Nanoparticles for Enhanced Methanol Oxidation Efficiency

Palladium nanocrystals immobilized on boron and nitrogen codoped mesoporous carbon spheres as efficient methanol oxidation electrocatalysts

Composition-controlled Synthesis of Platinum and Palladium Nanoalloys As Highly Active Electrocatalysts for Methanol Oxidation

Localization Of Platinum Nanoparticles On Inner Walls Of Mesoporous Hollow Carbon Spheres For Improvement Of Electrochemical Stability

One-step Synthesis of the PdPt Bimetallic Nanodendrites with Controllable Composition for Methanol Oxidation Reaction

Pt-content-controlled synthesis of Pd nanohollows/Pt nanorods core/shell composites with enhanced electrocatalytic activities for the methanol oxidation reaction