Manufacturing and degrading features of 3D-printed porous spinal interbody fusion cages
Zhiwei Jiao,Pengfei Chi,Hanlin Zou,Yuan Yu,Weimin Yang,Hao Liu,Dong Chen,Haibo Zou
DOI: https://doi.org/10.36922/ijb.1996
2024-03-05
International Journal of Bioprinting
Abstract:Spinal fusion operations are often utilized to address disc degeneration, vertebral slippage, instability, and trauma, and interbody fusion cages have been widely employed in these procedures. The fundamental aim of an interbody fusion cage is to give immediate interbody support, height, and biomechanical stability of the spinal space to enable bone development in the fused area. With the aim to address shortcomings of the currently commonly used clinical spinal interbody fusion cages, such as non-osteogenic activity, non-resorbability, biomechanical mismatch, etc., composites made of polycaprolactone (PCL) were prepared in this study, with the addition of hydroxyapatite (HA) that possesses both osteoinductive properties and enhanced mechanical strength as a functional filler. An innovative bi-directional variable meso-structure scheme is proposed. The porous degradable spinal interbody fusion cage was manufactured by using polymer melt differential three-dimensional (3D) printing technology. The study of the cage’s 3D structural characteristics on the degradation properties and the influence of the degradation process on its mechanical properties was carried out. Preliminary cell viability assays were also conducted. This study showed that the compressive strength of the cages increases with the aperture diameter and the number of crossing layers of the beams, and the compressive modulus is positively associated with the number of crossing layers of the beams. The degradation rate of the cage grew with the reduction of its filling rate and the rise of the number of crossing layers of the beams, i.e., the degradation rate increased with the expansion of the internal aperture. The cage with a 60% internal filling rate and containing 1 or 2 crossing layers of beams is more suited for spinal fusion, and with a pore size between 450 and 490 μm, the fundamental structure of the cage can be preserved while maintaining strong support performance throughout degradation. In addition, the 3D printing process in this study does not cause an increase in cytotoxicity, making it a feasible bioprinting method.
engineering, biomedical,materials science, biomaterials