Abstract:The electrochemical activity of thermo-decomposed Ti/IrO2 electrodes in aqueous solution containing methanol compound has been studied, emphasizing on the influence of calcination temperature. Scanning electron microscopy (SEM) images showed that the typical cracked morphology of oxide coatings disappears gradually as the preparation temperature increases, leading to the decrease in the amount of electrochemically active sites as measured by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) in organics-free aqueous solution. With the exception of samples prepared at high temperatures (e.g. 600°C), same change tendency of electro-activity with temperature was also found in methanol aqueous solutions, in which activity was observed to decrease as compared with that in blank solution. Three possible explanations for this phenomenon (i.e. active dissolution of oxide coatings, organics adsorption and dimerization/polymerization on electrode surface, respectively) were discussed, where the former two were believed to be more reasonable considering the CH3OH small molecular chosen in this system. However, none of these three mechanisms could explain the abnormal activation behavior observed at electrodes prepared at 600°C in CH3OH solution. XRD pattern showed the fact that when sintering temperature went up to 600°C IrO2 would decompose into metallic iridium component. The existence of metallic iridium might facilitate the organics oxidation as stated in previous literatures, which leads to the exceptional activation of oxide surface by methanol component. A simple reaction mechanism for electrodes in methanol aqueous solutions was proposed and used to interpret the negative shift in startness potential of the oxygen evolution reaction (OER). Organics oxidation seems to facilitate the OER and vice versa. The latter statement has been reported by other workers.

Effects of calcination temperature on component of TiO2 nanofibers and Pt/TiO2 nanofiber catalysts for methanol electrooxidation

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Preparation of Pt/TiO2 Nanofibers and Their Electrocatalytic Activity towards Methanol Oxidation

Preparation of Pt/TiO<sub>2</sub> Nanofibers and Their Electrocatalytic Activity Towards Methanol Oxidation

Effect of Calcination Temperature on Formaldehyde Oxidation Performance of Pt/TiO 2 Nanofiber Composite at Room Temperature

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

Effects of Calcination Temperature and CeO2 Contents on the Performance of Pt/CeO2−CNTs Hybrid Nanotube Catalysts for Methanol Oxidation

Preparation and Characterization of Pt/TiO 2 Nanofibers Catalysts for Methanol Electro-Oxidation

Preparation of TiO2 Nanofibres and Influence of Calcination Temperature on Photocatalytic Activity

Effects of CeO2 Pre-Calcined at Different Temperatures on the Performance of Pt/CeO2-C Electrocatalyst for Methanol Oxidation Reaction

Effect of TiO2 Calcination Pretreatment on the Performance of Pt/TiO2 Catalyst for CO Oxidation.

Effect of Heat Treatment on the Performance of TiO2-Pt/CNT Catalysts for Methanol Electro-Oxidation

The Effect of TiO 2 on the Catalytic Activity of a PtRu/C Catalyst for Methanol Oxidation

Effect of Calcination Temperature on Electrocatalytic Activities of Ti/IrO2 Electrodes in Methanol Aqueous Solutions

Carbon nanotubes/tin oxide nanocomposite-supported Pt catalysts for methanol electro-oxidation.

Effects of Calcination Condition on the Structure and Denitrification Performance of NiO/TiO_2 Catalyst

Effect of Calcination Temperature on the Structure, Crystallinity, and Photocatalytic Activity of Core-Shell SiO2@TiO2 and Mesoporous Hollow TiO2 Composites

Amorphous TiOx Stabilized Intermetallic Pt3Ti Nanocatalyst for Methanol Oxidation Reaction.

The effects of atmosphere and calcined temperature on photocatalytic activity of TiO 2 nanofibers prepared by electrospinning

Study on Synthesis of Pt/TiO2-NTs and the Mechanism for Methanol Electro-oxidation

Effect of Calcination Temperature on the Structure and Performance of Mn/Al2O3-TiO2 Catalyst in the Catalytic Oxidation of NO