Optical characteristics of Er3+ ion in Er/Yb: LiNbO3 crystal: Comparison with the dissimilar effect of anti-photorefractive ions Zn2+, In3+ and Zr4+
Yannan Qian,Rui Wang,Biao Wang,Chao Xu,Wei Xu,Lili Xing,Yanling Xu
DOI: https://doi.org/10.1016/j.jqsrt.2013.05.031
IF: 2.342
2013-01-01
Journal of Quantitative Spectroscopy and Radiative Transfer
Abstract:The different influences of Zn2+, In3+ and Zr4+ ions on the optical characteristics of Er3+ ion in Er/Yb:LiNbO3 crystals were discussed. An enhanced 1.54μm emission was observed for Zr/Er/Yb:LiNbO3 crystal, but the Zn2+ tri-doping resulted in a decreased one, and the intensity of 1.54μm emission remained about same in In/Er/Yb:LiNbO3 crystal. The populations of the green emitting 4S3/2/2H11/2 states were achieved through the three-, two- and two-phonon processes in Zn/Er/Yb:LiNbO3, In/Er/Yb:LiNbO3 and Zr/Er/Yb:LiNbO3 crystals, respectively. Zn2+ and In3+ ions affected the optical characteristics of Er3+ ion via modifying the Er3+ ion occupancy in Er/Yb:LiNbO3 crystal. The formation of ErLi2+–ErNb2− ion pairs caused by the Zn2+ and In3+ ions could increase the rate of cross relaxation process. The OH− absorption spectra showed that the incorporation of Zr4+ ions increased OH− content, which increased the probability of the nonradiative relaxation process of 4I11/2→4I13/2 (Er) in Zr/Er/Yb:LiNbO3 crystal. The J–O intensity parameters Ωt (t=2, 4 and 6), the radiative lifetime (τrad) and fluorescence branching ratio (β) in Zr/Er/Yb:LiNbO3 crystal were predicted by Judd–Ofelt theory. Füchtbauer–Ladenburg and McCumber methods were carried out to calculate the emission cross-sections at 1.54μm emission. The gain cross-section, estimated as a function of the population inversion ratio, allowed us to evaluate a potential laser performance of Zr/Er/Yb:LiNbO3 crystal.