Effect of Microstructures on Fatigue Crack Growth Behavior of Friction Stir Processed NiAl Bronze Alloy

Yuting Lv,Yang Ding,Yuanfei Han,Laizhi Wu,Liqiang Wang,Weijie Lu

DOI: https://doi.org/10.1007/s11661-016-3937-1

2017-01-01

Metallurgical and Materials Transactions A

Abstract:: Friction stir processed (FSPed) NAB alloy exhibits inhomogeneous microstructures that can be divided into three subregions from the top surface to the bottom according to α phase morphologies: Widmanstatten α subregion, banded α colonies, and stream-like α colonies. In this study, a constant stress intensity range (Δ K ) was used for each sample to study the effect of microstructures on the fatigue crack growth rate (FCGR) of FSPed NAB alloy. The results show that α phase in banded and stream-like α colonies experiences completely dynamic recrystallization and forms equiaxed α grains during FSP. The FCGR of FSPed NAB alloy continuously decreases from the top surface to the bottom. In the subregion with stream-like α colonies, the alloy containing a higher content of equiaxed α grains and fine κ iv phase, and less retained β ( β ′) phase exhibits the best FCG resistance. The equiaxed α grains deflect the main crack and increase crack tortuosity effect, which make a main contribution to FCG resistance of FSPed NAB alloy, while martensite β ′ phase produced during FSP accelerates its fatigue crack growth. Compared to matrix alloy, FSPed NAB alloy exhibits better FCG resistance only at high Δ K levels. At low Δ K levels, the crack deflection effect caused by coarser κ phase in the matrix alloy obviously improves its FCG resistance. With the increasing Δ K , the aforementioned crack deflection effect gradually diminishes and fatigue crack prefers to propagate in a flat way, resulting in higher FCGR of matrix alloy.