Nanostructured porous WO 3 for photoelectrochemical splitting of seawater
M. Parvin,Irena Savickaja,S. Tutliene,Arnas Naujokaitis,Rimantas Ramanauskas,Milda Petrulevičienė,Jurga Juodkazytė
DOI: https://doi.org/10.2139/ssrn.4579217
IF: 4.598
2024-01-12
Journal of Electroanalytical Chemistry
Abstract:Seawater, due to its salinity, can serve as an electrolyte in photoelectrochemical (PEC) systems, which have the potential to enable solar-driven production of hydrogen and oxidizing species. In this study several micrometer thick and highly porous nanostructured WO 3 films were formed and their performance in photoanodic oxidation of chloride and sulfate ions, the most abundant anionic species in seawater, was investigated. Layers were characterized using scanning electron microscopy, X-ray diffraction, diffuse reflectance spectroscopy, and BET surface area measurements. The study demonstrates that efficient PEC performance is achieved through optimal light absorption by sufficiently thick WO 3 layers (3–5 μm), a highly porous structure that facilitates electrolyte permeation and ionic transport and provides a large electrochemically active interfacial area, and a nanosheet morphology where the sheet thickness is shorter than the hole diffusion length in WO 3 . The Faradaic efficiency of ClO - + ClO 2 - generation in neutral chloride-based electrolytes was found to be close to 100 %, but decreased significantly with photoelectrolysis time, presumably, due to the formation of higher chlorine oxo compounds. In addition, photocurrent stability and dissolution of WO 3 photoanodes in acidic sulfate and neutral chloride media was compared. Though dissolution of WO 3 in 0.5 M NaCl was found to be up to 3 times higher, photocurrent decay was more significant in 0.5 M H 2 SO 4 . The phenomenon was attributed to effective hole scavenging by surface-adsorbed Cl - ions, which prevents passivation of the photoelectrode surface due to formation of W(VI) peroxospecies.
chemistry, analytical,electrochemistry