Atomic Structure and Migration Dynamics of MoS2/LixMoS2 Interface

Shulin Chen,Liping Wang,Ruiwen Shao,Jian Zou,Ran Cai,Jinhuang Lin,Chongyang Zhu,Jingmin Zhang,Feng Xu,Jian Cao,Jicai Feng,Junlei Qi,Peng Gao
DOI: https://doi.org/10.1016/j.nanoen.2018.03.076
IF: 17.6
2018-01-01
Nano Energy
Abstract:The performance of alkali-metal-ion batteries largely depends on the migration behavior of alkali metal ions in the electrodes. Probing the atomic structure of the reaction interface and the dynamic process during ion transport in the electrodes will help better understand the underlying electrochemical mechanisms and inspire rational electrode designs. In this study, by combining in situ transmission electron microscopy (TEM) and aberration-corrected scanning TEM (STEM), we track the reversible lithium ion transport in MoS2 nanostructures to reveal the atomic structure and dynamic behaviors of the reaction interface. We find that lithium ions insertion triggers complex phase transformations. Three different phases co-exist at the interface: a pristine 2H phase, a 1T phase with a shrank lattice constant of -3.3% (+/- 2.3%), and a distorted 1T phase (called 1T' phase) with an expanded lattice constant of 5.5% (+/- 2.5%). The atomically resolved Z-contrast image shows that the expanded 1T' phase has distorted Mo arrangements. Furthermore, the lithium ions migration causes defects at the reaction front, and the diffusion on the surface is faster than that inside, forming a core-shell structure at the reaction interface. The diffusivity of lithium ions is directly measured to be similar to 1000-30,000 nm(2)/s, which is significantly higher than that of sodium insertion (similar to 10-20 nm(2)/s). The atomic-scale observations of lithium-ion-migration-induced complex structural evolutions would help understand the properties of MoS2 nanostructures and shed light on the design of alkali-metal-ion batteries with general transition-metal dichalcogenide electrodes.
What problem does this paper attempt to address?