Iridium Nanoparticles Anchored on 3D Graphite Foam As a Bifunctional Electrocatalyst for Excellent Overall Water Splitting in Acidic Solution

Jian Zhang,Gang Wang,Zhongquan Liao,Panpan Zhang,Faxing Wang,Xiaodong Zhuang,Ehrenfried Zschech,Xinliang Feng
DOI: https://doi.org/10.1016/j.nanoen.2017.07.054
IF: 17.6
2017-01-01
Nano Energy
Abstract:The proton-exchange-membrane (PEM) water-splitting electrolyser is a highly appealing technology for economical hydrogen production. Unfortunately, only Iridium (Ir)-based electrocatalysts show efficient and stable activity towards oxygen evolution reaction (OER) in acidic medium, which seriously hampers the large-scale utilization of PEM water splitting electrolyser as a result of high cost and scarcity of the Ir. Here, we report synthesis of Ir nanoparticles on 3D graphite foam (Ir/GF) upon a heat treatment of Ir3+/polyaniline complex that were beforehand prepared on the GF. Benefiting from low content of Ir (5.91wt%) and excellent resistance of 3D graphite foam against oxidative corrosion, the resultant Ir/GF functionalizes as a novel bifunctional electrocatalyst for overall water splitting in a 0.5M H2SO4 solution. Noticeably, the HER and OER overpotentials of the Ir/GF at 10mA/cm2 are only ~ 7mV and ~ 290mV, respectively, which are much lower than those of commercial Pt/C and Ir/C catalysts as well as reported Pt or Ir-based electrocatalysts. Significantly, an acidic water-splitting electrolyser with a current density of 10mA/cm2 is steadily driven by the Ir/GF at a cell voltage of only ~ 1.55V, which is substantially lower than 1.65V for commercial Pt/C and Ir/C couple.
What problem does this paper attempt to address?