Hybrid Electrodes Based on Zn–Ni–Co Ternary Oxide Nanowires and Nanosheets for Ultra-High-Rate Asymmetric Supercapacitors
Jiwan Acharya,Tae Hoon Ko,Jae-Gyoung Seong,Min-Kang Seo,Myung-Seob Khil,Hak-Yong Kim,Byoung-Suhk Kim
DOI: https://doi.org/10.1021/acsanm.0c01419
IF: 6.14
2020-08-25
ACS Applied Nano Materials
Abstract:In this study, hydrolysis agent-assisted three-dimensional (3D) flowerlike hierarchical zinc–nickel–cobalt oxide (ZNCO) nanostructured materials, which consist of two-dimensional (2D) ZNCO nanosheets anchored with one-dimensional (1D) ZNCO nanowire architectures, as binder-free electrodes for ultrahigh-rate supercapacitor applications are directly fabricated on Ni foam via a facile hydrothermal method followed by calcination. The morphologies of the as-fabricated flowerlike 3D hierarchical ZNCO nanostructures dramatically depend on the combination method (urea, hexamethylenetetramine, hexamethylenetetramine–urea) of the hydrolysis reagents used, which are denoted ZNCO-U, ZNCO-H, and ZNCO-HU, respectively. Among them, the as-prepared ZNCO-HU electrode shows outstanding electrochemical performance with a higher specific capacity of 259.8 mAh g–1 at 1 A g–1, ultrahigh capacitance retention of 83.9% at a higher current density of 50 A g–1, and remarkable long cycle stability over 5000 cycles. The assembled asymmetric supercapacitor (ASC) device using ZNCO-HU as the cathode and N-doped graphene hydrogel (NGH) as the anode materials delivers a noticeable specific capacity of 76.5 mAh g–1 at 1 A g–1 and good rate capability of 69.65% at 10 A g–1. The sandwiched ASC displays a superior energy density of 55.4 Wh kg–1 at a power density of 761.5 W kg–1 and excellent capacity retention of 89% up to 5000 cycles.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsanm.0c01419.EDX spectrum of the ZNCO-HU flowerlike superstructures and elemental mapping of different elements (Figure S1); XRD pattern of the ZNCO-HU precursor before calcination (Figure S2); electrochemical performance for the ZNCO-U electrode, CV curves for ZNCO-U at different scan rates, and GCD curves for the ZNCO-U electrode at different current densities (Figure S3); electrochemical performance for the ZNCO-H electrode, CV curves for ZNCO-H at different scan rates, and GCD curves for the ZNCO-H electrode at different current densities (Figure S4); cyclic performance for the ZNCO flowerlike superstructures prepared using three different reagents at 20 A g–1 (Figure S5); FE-SEM images of ZNCO-HU after consecutive 5000 charge/discharge cycles (Figure S6); FE-SEM images, CV curves, GCD curves, rate performance, and Nyquist plot for the NGH as an anode material (Figure S7); and areal capacitance of the ZNCO-HU electrode at various scan rates from 5 to 200 mV s–1 (Figure S8) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology