Abstract:The original phase-pure M1 MoVNbTeOx catalyst was mechanically treated with stirring water for several days under ambient conditions to obtain particles with different sizes. The catalytic performance was sig-nificantly improved and stabilized after about 7 days of treatment. Among all the catalysts, the sample treated in water for 7 days can obtain 57.6 % ethane conversion and 0.79 kgC2H4/kgcat/h ethylene produc-tivity while the original phase-pure M1 catalyst was only 19.2 % and 0.27 kgC2H4/kgcat/h at reaction tem-perature of 400 degrees C and contact time of 18.5 gcat center dot h/molC2H6. Meanwhile, the catalyst was systematically characterized and the results showed that there was essentially no difference in microstructure between the original and treated catalysts. TEM and SEM morphological characterizations presented that the par-ticle size and aspect ratio of the catalysts changed significantly, in which the particle size of the catalyst become smaller and the proportion of basal surface was enhanced. The activity and selectivity of the cat-alysts exhibited a correlation with the amount and proportion of basal surface. It can be deducted that the basal surface is the most active and selective surface during oxidative dehydrogenation of ethane (ODHE) process, and the intrinsic activity based on the basal (001) plane of the catalyst remains stable after the mechanical treatment. Samples treated in water for 7 days showed excellent long-term stability in a 200 h stability test at reaction temperature of 440 degrees C and contact time of 9.3 gcat center dot h/molC2H6. The present work demonstrated that the differences in the catalytic properties of different M1 samples depend mainly on the amount and proportion of exposed basal surface, and the possibility of enhancing the activ-ity of orthorhombic M1 phase by fragmentation method.(c) 2022 Elsevier Inc. All rights reserved.

Study of the thermal evolution of super-efficient defective MoVSbOx catalyst used for ethane oxidative dehydrogenation by In-situ HAADF-STEM Electron Tomography

Microporous Exposure on Catalytic Performance of MoVNbTeOx Mixed Metal Oxides in the Oxidative Dehydrogenation of Ethane

Determination of Highly Active and Selective Surface for the Oxidative Dehydrogenation of Ethane over Phase-Pure M1 Movnbteox Catalyst

Better Catalysts through Microscopy: Mesoscale M1/M2 Intergrowth in Molybdenum-Vanadium Based Complex Oxide Catalysts for Propane Ammoxidation.

Mixed Metal Oxides of M1 MoVNbTeOx and TiO2 As Composite Catalyst for Oxidative Dehydrogenation of Ethane

Catalytic Performance of Phase-Pure M1 MoVNbTeOx/CeO2 Composite for Oxidative Dehydrogenation of Ethane

Influence of the Content and Distribution of Vanadium in the M1 Phase of the MoVTe(Sb)NbO Catalysts on their Catalytic Properties in Light Alkanes Oxidation

MnO Promoted Phase-Pure M1 MoVNbTe Oxide for Ethane Oxidative Dehydrogenation

Alternative Mechanisms for Translesion Dna Synthesis

Olefin Metathesis over Heterogeneous Catalysts: Interfacial Interaction Between Mo Species and a Hβ−Al2O3 Composite Support

Phase-pure M1 MoVNbTeOx Catalysts with Tunable Particle Size for Oxidative Dehydrogenation of Ethane

Nanocomposite Catalysts of Non-Purified MoVNbTeOx with CeO2 or TiO2 for Oxidative Dehydrogenation of Ethane

Insights into the Deactivation Mechanism of Heterogeneous Mo/H Beta-Al2o3 Catalysts for Olefin Metathesis

Performance of phase-pure M1 MoVNbTeOx catalysts by hydrothermal synthesis with different post-treatments for the oxidative dehydrogenation of ethane

MoVNbTeOx M1@CeO2@Cordierite Structured Catalysts for ODHE Process

Multinuclear solid-state NMR characterization of the coke on Mo/Hβ-Al2O3 catalyst for olefin metathesis

Characterization and Evaluation of MoVTeNb Mixed Metal Oxide Catalysts Fabricated Via Hydrothermal Process with Ultrasonic Pretreatment for Propane Partial Oxidation

Phase-pure M1 MoVNbTeOx/TiO2nanocomposite Catalysts: High Catalytic Performance for Oxidative Dehydrogenation of Ethane

Continuous Flow Hydrothermal Synthesis of MoVNbTeOx in Micro-Coil Tubular Reactor for Oxidative Dehydrogenation of Ethane

Identification of the Intrinsic Active Site in Phase-Pure M1 Catalysts for Oxidation Dehydrogenation of Ethane by Density Functional Theory Calculations

Investigation of Deoxidation Process of MoO3 Using Environmental TEM