Enhanced Electrocatalytic Hydrogen Evolution from Large-Scale, Facile-Prepared, Highly Crystalline WTe 2 Nanoribbons with Weyl Semimetallic Phase.

Jie Li,Meiling Hong,Leijie Sun,Wenfeng Zhang,Haibo Shu,Haixin Chang

DOI: https://doi.org/10.1021/acsami.7b13387

IF: 9.5

2018-01-01

ACS Applied Materials & Interfaces

Abstract:WTe2 is one of most important layered transition metal dichalcogenides (TMDs) and exhibits various prominent physical properties. All the present methods for WTe2 preparation need strict conditions such as high temperature or cannot be applied in large scale which limit the practical applications. In addition, most studies on WTe2 focus on its physical properties while the electrochemical properties are still illusive with little investigation. Here we develop a facile and scalable two-step method to synthesize high quality WTe2 nanoribbon crystal with 1T'Weyl semimetal phase for the first time. We can get highly crystalline 1T'-WTe2 nanoribbon on a large scale through this two-step method. In addition, the electrochemical tests show that WTe2 nanoribbon exhibits smaller overpotential and much better hydrogen evolution reaction (HER) catalytic performance than other tungsten-based sulfide and selenide (WS2, WSe2) nanoribbons under same morphology and preparation condition. WTe2 nanoribbons show a Tafel slope of 57 mV/dec, which is one of best values for TMDs catalysts and about 2 and 4 times smaller than that 135 mV/dec for 2H-WS2 nanoribbon and 213 mV/dec for 2H-WSe2 nanoribbon, respectively. 1T'-WTe2 nanoribbon also show ultrahigh stability in 5000 cycles and 20 h at 10 mA/cm2. The better performance is attributed to high conductivity of semimetallic 1T'-phase-stable WTe2 nanoribbon with one or two order higher charge transfer rate than normally semiconducting 2H-stable WS2 and WSe2 nanoribbons. These results open the door of electrochemical applications of Weyl semimetallic TMDs.