Abstract:Cryptomelane-type MnO2 nanomaterials with a-crystalline phase were prepared by heat treatment of the mixture of MnCO3 and potassium oxalate followed by acid treatment. The evolution of the crystalline phase and morphology from MnCO3 to cryptomelane was investigated by XRD, BET, SEM and TEM. Moreover, MnO2 in nanoparticle, nanorod and nanofiber shapes could be controlled by adjusting the reaction time and temperature in the acid-treatment step. MnO2 nanofibers demonstrated promoted catalytic activity and recyclability for the oxidative degradation of various organic dyes, tetracyclines and bisphenol A via peroxymonosulfate (PMS) activation. About 99% of RhB, AO7, MB, red 2 and bisphenol A at a concentration of 20–50 mg/L could be degraded over MnO2 nanofibers within 12 min. Furthermore, antibiotics, like tetracycline, chlortetracycline and oxytetracycline, and bisphenol A could be mineralized efficiently, and 69–81% TOC removal was obtained. Compared to MnO2 nanowires synthesized by the traditional method with KMnO4, MnO2 nanofibers showed enhanced surface area (102 m2/g), more labile lattice oxygen species and higher oxygen vacancy content, which might be responsible for the superior catalytic performances. The radical quenching test and EPR analysis proved that radical (O2−, SO4− and OH) and non-radical (1O2) processes both existed, and the latter dominantly contributed to the degradation. Based on kinetic study, the activation energy of MnO2 nanofibers/PMS for RhB degradation was only 10.55 kJ/mol, which was lower than that of MnO2 nanowires (16.80 kJ/mol). This study not only offered a new, simple and economical protocol for the scaled-up synthesis of nano-scale MnO2 materials, but also demonstrated its potential in water remediation.

Synthesis of MnO2 Nanosheets on Montmorillonite for Oxidative Degradation and Adsorption of Methylene Blue

Adsorption of Methylene Blue by Halloysite/MnFe2O4 Nanocomposites

Photothermal Effect Improving the Activity of Spinel MnFe2O4 Nanoparticles for the Catalytic Activation HCO3−/H2O2 to Achieve the Degradation of Dye Pollutants in Low-Temperature Condition

Oxidative degradation of aqueous organic contaminants over shape-tunable MnO2 nanomaterials via peroxymonosulfate activation

Preparation of MnO_2 Nanorod and Its Catalytic Performance

Manganese Oxyhydroxide And Oxide Nanofibers For High Efficiency Degradation Of Organic Pollutants

Adsorption Behavior and Mechanism of Fe-Mn Binary Oxide Nanoparticles: Adsorption of Methylene Blue.

Degradation of Bisphenol A by Nano-Sized Manganese Dioxide Synthesized Using Montmorillonite As Templates

Synthesis and characterization of montmorillonite – Mixed metal oxide composite and its adsorption performance for anionic and cationic dyes removal

Facile synthesis of MnO2/g-C3N4 for photocatalytic reduction of methylene blue dye under visible light

SYNTHESIS, CHARACTERIZATION OF MN3O4: ADSORPTION APPLICATION AND ANTIBACTERIAL EVALUATION

Carboxymethyl cellulose assisted morphology controlled synthesis of Mn3O4 nanostructures for adsorptive removal of malachite green from water

Facile and template-free preparation of α-MnO2 nanostructures and their enhanced adsorbability

Facile synthesis of 2D α-MnO 2 nanosheets for the removal of heavy metal ions

Biomimetic preparation of MoS2-Fe3O4 MNPs as heterogeneous catalysts for the degradation of methylene blue

MoO2 nanostructures synthesized via hydrothermal method for enhanced Methylene blue decontamination

Study on degradation of acid orange II in aqueous solution using one-dimensional MnO(2) nanorods

Adsorption of Methylene Blue on Azo Dye Wastewater by Molybdenum Disulfide Nanomaterials

Construction of K and Tb Co-doped MnO2 nanoparticles for enhanced oxidation and detoxication of organic dye waste

Phase tunable nickel doped Mn3O4 nanoparticle synthesis by chemical precipitation: kinetic study on dye degradation

Synthesis of MnO2/g-C3N4 nanocomposite for the efficient photocatalytic degradation of methylene blue and acid blue 113 dyes