Photo‐Induced Construction and Recovery of Cu+ Sites in Metal–Organic Frameworks
Yu‐Xia Li,Ke‐Di Li,Xin‐Yu Qian,Xiao‐Qin Liu,Lin‐Bing Sun
DOI: https://doi.org/10.1002/smll.202302885
IF: 13.3
2023-06-02
Small
Abstract:Cu+ species are able to selectively capture unsaturated molecules due to the π‐complexation, while it is easily oxidized to Cu2+, resulting in the loss of such an ability. This work demonstrates that a facile photo‐induced strategy is effective in not only the construction of Cu+ sites in a metal–organic framework but also their reversible recovery from the oxidized counterparts. The adjustment of the valence state of metal ions is crucial for various applications because peculiar activity originates from metal ions with specific valence. Cu+ can interact with molecules possessing unsaturated bonds like CO via π‐complexation, while Cu2+ doesn't have such ability. Meanwhile, Cu+ sites are easily oxidized to Cu2+, leading to the loss of activity. Despite great efforts, the development of a facile method to construct and recover Cu+ sites remains a pronounced challenge. Here, for the first time a facile photo‐induced strategy is reported to fabricate Cu+ sites in metal–organic frameworks (MOFs) and recover Cu+ after oxidation. The Cu2+ precursor was loaded on NH2‐MIL‐125, a typical visible‐light responsive Ti‐based MOF. Visible light irradiation triggers the formation of Ti3+ from Ti4+ in framework, which reduces the supported Cu2+ in the absence of any additional reducing agent, thus simplifying the process for Cu+ generation significantly. Due to π‐complexation interaction, the presence of Cu+ results in remarkably enhanced CO capture capacity (1.16 mmol g−1) compared to NH2‐MIL‐125 (0.49 mmol g−1). More importantly, Cu+ can be recovered conveniently via re‐irradiation when it is oxidized to Cu2+, and the oxidation‐recovery process is reversible.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology