P-Type Cobalt Phosphide Composites (CoP–Co 2 P) Decorated on Titanium Oxide for Enhanced Noble-Metal-Free Photocatalytic H 2 Evolution Activity
Rong Liang,Yanwen Wang,Chao Qin,Xuehua Chen,Zhizhen Ye,Liping Zhu
DOI: https://doi.org/10.1021/acs.langmuir.0c03362
IF: 3.9
2021-03-11
Langmuir
Abstract:Nowadays, transition-metal phosphides have been reported to function well in photocatalytic water splitting and possess great potential to substitute traditional noble-metal cocatalysts in the future. Herein, p-type cobalt phosphide (CoP–Co<sub>2</sub>P) nanomaterials were synthesized by phosphating the solvothermally prepared Co(OH)<sub>2</sub> nanoflowers at a low temperature (300 °C). Then, we combined the phosphides with commercial TiO<sub>2</sub> through facile mechanical mixing to fabricate a useful noble-metal-free photocatalyst. The phosphating time that had an influence on the composition of phosphides was tuned, and 3 h was an ideal condition after comparison. The cobalt phosphide-modified TiO<sub>2</sub> at the optimal weight percentage (nominal 0.5%) exhibited the highest photocatalytic hydrogen rate of approximately 824.5 μmol g<sup>–1</sup> h<sup>–1</sup> under simulated sunlight irradiation, which was nearly equal to 160 times that of bare TiO<sub>2</sub> and 1.7 times that of single CoP-modified TiO<sub>2</sub>. The CoP<sub><i>x</i></sub>/TiO<sub>2</sub> heterojunction interfaces were studied using photoluminescence (PL), time-resolved PL, and photoelectrochemical methods, which revealed that the effective charge separation and transfer accelerated by the built-in electric field of p–n junction contributed significantly to the photocatalytic performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c03362?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c03362</a>.XRD of CoP<sub><i>x</i></sub> with different phosphorization parameters (time and temperature); SEM, TEM, and HRTEM of CoP and CoP<sub><i>x</i></sub>; SEM and XRD of Co(OH)<sub>2</sub>; characterizations of TiO<sub>2</sub> (SEM and XRD) and 0.5-CoP/TiO<sub>2</sub> (SEM, XRD, and TEM); SEM, XRD, and XPS of 0.5-CoP<sub><i>x</i></sub>/TiO<sub>2</sub> before and after the cyclic test; cyclic test and AQY test of 0.5-CoP<sub><i>x</i></sub>/TiO<sub>2</sub>; H<sub>2</sub> evolution test of CoP<sub><i>x</i></sub>/TiO<sub>2</sub> from different phosphorization time; Mott–Schottky plots of CoP, CoP<sub><i>x</i></sub>, TiO<sub>2</sub>, and 0.5-CoP<sub><i>x</i></sub>/TiO<sub>2</sub>; VBM spectrum of TiO<sub>2</sub>; zeta potentials of P25 and CoP<sub><i>x</i></sub>; and ICP-AES of CoP<sub><i>x</i></sub> and CoP (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c03362/suppl_file/la0c03362_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary, physical,materials science