Novel nanocomposite made of calcium zinc silicate/ NiO 2 for biomedical applications

H.H.A. Sherif,E.M.A. Hamzawy,I.K. El Zawawi,S.H. Kenawy,Gehan T. El-Bassyouni,Manal A. Mahdy

DOI: https://doi.org/10.1016/j.ceramint.2024.01.155

IF: 5.532

2024-02-23

Ceramics International

Abstract:The novel nanocomposites of ZnO-containing CaSiO 3 /NiO 2 were prepared through the wet precipitation method. The XRD of samples sintered at 1100 °C/2 h presented variable phases, mainly hardystonite (Ca 2 ZnSi 2 O 7 ) with two secondary phases of willemite (Zn 2 SiO 4 ) and tridymite (SiO 2 ). Similarly, small diffraction peaks of peroxide nickel oxide (NiO 2 ) arose in samples containing significant concentrations of it. All composites were crystallized in the nano-range, and their particle sizes (Ps) range from 60 to 70 nm. According to the morphological investigation, the percentage of NiO 2 increased grain size. The optical result assured that the willemite phase has an optical band gap of 5.35–5.58 eV and a minor transition at ∼3.4 eV. While NiO 2 had a small transition found at 1.7 ± 0.05 eV. The lattice vibrations of Ca–O, the stretching of the C–O group in CaCO 3 , and the Si–O symmetric stretching were affected by the NiO 2 concentration, as evident from the Raman spectra. Nevertheless, the FTIR result revealed that the increasing NiO 2 concentration did not affect the stretching and bending vibrations of the composites. The values of moment/g increased with NiO 2 , and two magnetic contributions were revealed. The concentration of NiO 2 in the composite was shown to be connected to the composite's ability to suppress the various microbiological strains tested. There is no detectable inhibitory impact when the sample's NiO 2 content is less than 3%. This research topic provides an opportunity to look into novel materials with possible antimicrobial uses for infection prevention in biological fields, such as bone repair.

materials science, ceramics