Improved Performance of Perovskite Solar Cell by Controlling CH 3 NH 3 PbI 3−x Cl X Film Morphology with CH 3 NH 3 Cl-assisted Method

B. G. Zhao,L. Zhu,Y. L. Zhao,Y. Yang,J. Song,X. Q. Gu,Z. Xing,Y. H. Qiang

DOI: https://doi.org/10.1007/s10854-016-5196-8

2016-01-01

Journal of Materials Science Materials in Electronics

Abstract:Sequential deposition solution-based method has been widely used for the fabrication of perovskite solar cells (PSCs). However, there is still a challenge to achieve homogeneous and consecutive surface of the perovskite layers. In this work, CH3NH3PbI3−xClx layers were prepared by a modified two-step solution method. Specifically, the optimum amount of CH3NH3Cl pre-added into PbI2 precursor solution, the appropriate size of pinholes and voids appear in PbI2 films and leave room for the growth of CH3NH3PbI3−xClx crystal. Under this condition, the crystal grains size is diminished and the surface coverage ratio of CH3NH3PbI3−xClx film is enhanced, which prevent the combination of electron-hole pairs on the interface between perovskite layer and TiO2 substrate. By varying the CH3NH3Cl amounts, the PSC devices displayed the highest power conversion efficiency of 13 %, which was obviously higher than that of the one prepared via transitional routes (10.32 %). As a result, we developed a simple and repeatable route for controllable synthesis of perovskite absorption layers, which is demonstrated to be effective to improve the performance of PSCs.