Abstract:We have attempted to develop surface-enhanced Raman scattering (SERS) substrates by the use of two-dimensional (2D) Au nanorod arrays and to characterize the SERS-active sites of the Au nanostructures. We prepared two different types of 2D Au nanorod arrays by means of the anodic aluminum oxide (AAO) template-assisted nanofabrication. In the template-embedded array (type I) an Au nanorod fills up the AAO pore, while in the annularly spaced array (type II) an Au nanorod keeps similar to 20 mn away from the pore wall. The strongest SERS effect was observed for both types of substrates with an Au nanorod diameter of similar to 66 nm. With respect to the bare AAO template, the NaOH-etched (unetched) type I substrate with the 66 nm Au nanorod showed 115-fold (63-fold) enhancement in Raman scattering, corresponding to a SERS enhancement factor of 10(7) - 10(9). For the unetched and ordered Au naonorod arrays, the SERS-active sites localized around the rod end, whereas for the NaOH-etched and partially aggregated Au nanorods, hot spots for SERS were found in the interstices between rod tips. The type II substrate allowed the effect of rod length on the SERS response to be investigated, and the SERS response was observed to vary very little with the rod length increase (250-1000 nm), indicating that majority of the signal originates at the rod end. A comparison between the analytes all-trans-beta-carotene and pyridine suggests that, for both types of substrates, the electromagnetic enhancement is predominant over the chemical enhancement. This work demonstrates that the unetched type I substrate is highly SERS effective, for which the fabrication protocol is advantageous in its simplicity and reproducibility.

Ordered Hexagonal Nanoplasmonic Au Nanoparticle Arrays: AAO-Assisted Thermal Treatment Synthesis and Application As Surface-Enhanced Raman Scattering Substrates

Self-assembly of Au Nanoparticle Arrays by Porous Anodic Alumina Templates Leads to Surface-Enhanced Raman Scattering

Surface-Enhanced Raman Scattering from Au-Nanorod Arrays with Sub-5-nm Gaps Stuck Out of an AAO Template

Optical Field Enhancement in Au Nanoparticle-Decorated Nanorod Arrays Prepared by Femtosecond Laser and Their Tunable Surface-Enhanced Raman Scattering Applications.

Controlled assembly of highly Raman-enhancing silver nanocap arrays templated by porous anodic alumina membranes

Controlled Growth and Multi-Photon Luminescence of Hexagonal Arrays of Au Nanoparticles on Anodic Aluminum Oxide Templates

Anisotropic Nanoparticle Arrays Guided by Ordered Nanowire Films Enhance Surface‐Enhanced Raman Scattering

Surface Plasmon Resonance and Interference Coenhanced SERS Substrate of AAO/Al-Based Ag Nanostructure Arrays

Assembly Nanoparticle Arrays Decorated with Ultrathin AAO Nanopores for Highly Sensitive SERS Substrate

Effects of annealing temperature on morphological and optical properties of Ag nanoparticle array and its application in SERS

Silver nanostructure arrays abundant in sub-5 nm gaps as highly Raman-enhancing substrates

Aligned Copper Nanorod Arrays for Surface-Enhanced Raman Scattering

Controlled Fabrication Of Nanopillar Arrays As Active Substrates For Surface-Enhanced Raman Spectroscopy

Tunable Ordered Silver Nano-Arrays Prepared by TiO 2 Templates as Surface-Enhanced Raman Scattering Substrates

Silver Nanovoid Arrays for Surface-Enhanced Raman Scattering

Gold Nanorod Arrays With Good Reproducibility For High-Performance Surface-Enhanced Raman Scattering

Large-area Opposing Double Nanocrescents-Nanoparticle Arrays for Polarization Dependent SERS Effects

Tunable Silver Nanocap Superlattice Arrays for Surface-Enhanced Raman Scattering

A Three-Dimensional Surface-Enhanced Raman Scattering Substrate: Au Nanoparticle Supramolecular Self-Assembly in Anodic Aluminum Oxide Template

Facile Fabrication of Au Nanoparticles-Decorated Ni Nanocone Arrays As Effective Surface-Enhanced Raman Scattering Substrates

Fabrication of Hexagonally Patterned Flower-Like Silver Particle Arrays As Surface-Enhanced Raman Scattering Substrates