Phase Coexistence and High Electrical Properties in (kxna0.96−xli0.04)(nb0.85ta0.15)o3 Piezoelectric Ceramics
Yunfei Chang,Zupei Yang,Difei Ma,Zonghuai Liu,Zenglin Wang
DOI: https://doi.org/10.1063/1.3081643
IF: 2.877
2009-01-01
Journal of Applied Physics
Abstract:( K x Na 0.96 − x Li 0.04 ) ( Nb 0.85 Ta 0.15 ) O 3 lead-free piezoelectric ceramics were produced by conventional solid-state reaction method. The effects of K/Na ratio on the phase transitional behavior, Raman spectrum, microstructure, and dielectric, piezoelectric, and ferroelectric properties of the ceramics have been investigated. The phase structure of the ceramics undergoes a transition from orthorhombic to tetragonal phase with increasing x. A double-degenerate symmetric O–Nb–O stretching vibration v1 and a triply degenerate symmetric O–Nb–O bending vibration v5 are detected as relatively strong scattering in the Raman spectra. The peak shifts of v5 and v1 modes all have a discontinuity with x between 0.42 and 0.46, which may suggest the coexistence of orthorhombic and tetragonal phases in this range. Properly modifying x reduces the sintering temperature, promotes the grain growth behavior, and improves the density of the ceramics. The polymorphic phase transition (at To-t) is shifted to near room temperature by increasing x to 0.44 (K/Na ratio of about 0.85:1), and the coexistence of orthorhombic and tetragonal phases in the ceramics at x=0.44 results in the optimized electrical properties (d33=291 pC/N, kp=0.54, εr=1167, tan δ=0.018, To-t=35 °C, TC=351 °C, Pr=27.65 μC/cm2, and Ec=8.63 kV/cm). The results show that the equal K/Na ratio is not an essential condition in obtaining optimized electrical properties in (KxNa0.96−xLi0.04)(Nb0.85Ta0.15)O3 ceramics.