Abstract:A novel method for the preparation of hydrophilic and positively charged nanofiltration (NF) membranes was developed. An active top-layer with NF characteristic was composited onto polysulfone (PSf) ultrafiltration substrate by UV-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA) followed by quaternization cross-linking with p-xylylene dichloride (XDC). Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy and atomic force microscopy were employed to monitor membrane surface chemical and morphological changes after poly(DMAEMA) grafting and quaternization cross-linking. The influences of UV irradiation time, monomer DMAEMA concentration, the cross-linker XDC concentration on the separation and permeation properties of membrane were investigated. The surface hydrophilicity of the composite membranes was evaluated by contact angle measurement. It was found that membrane hydrophilicity was obviously enhanced after UV-induced grafting and quaternization cross-linking. As the UV irradiation time and DMAEMA monomer concentration were increased, salts rejection of the composite membranes increased while water permeability decreased. Under the optimized preparing conditions, water flux and MgCl2 rejection (1.0g/L) of the composite membranes reached 60.3L/(m2hMPa) and 93.2%, respectively. The membrane surface charge property was measured via a streaming potential method. It was found that, at pH from 4.5 to 9, the composite membranes showed positive zeta potentials. The rejections of the composite membranes to different salts followed the order Na2SO4<NaCl<MgSO4<MgCl2<CaCl2. Moreover, the composite NF membranes showed a good stability in water-phase filtration process.

Fabrication of Composite Nanofiltration Membranes by Dopamine-Assisted Poly(ethylene Imine) Deposition and Cross-Linking

Novel composite nanofiltration membranes containing zwitterions with high permeate flux and improved anti-fouling performance

Fabrication and performance of a new type of charged nanofiltration membrane based on polyelectrolyte complex

Fabrication anddye-salt separation of positively charged PVC/PEI composite nanofiltration membranes

A Novel Positively Charged Nanofiltration Membrane Formed Via Simultaneous Cross-Linking/quaternization of Poly(m-Phenylene Isophthalamide)/polyethyleneimine Blend Membrane

Characterization of a positively charged composite nanofiltration hollow fiber membrane prepared by a simplified process

Bioinspired fabrication of composite nanofiltration membrane based on the formation of DA/PEI layer followed by cross-linking

A Novel Thin-Film Nano-Templated Composite Membrane with in Situ Silver Nanoparticles Loading: Separation Performance Enhancement and Implications

An Acid Resistant Nanofiltration Membrane Prepared from a Precursor of Poly(s-Triazine-amine) by Interfacial Polymerization

Nanofiltration Membranes Via Co-Deposition of Polydopamine/polyethylenimine Followed by Cross-Linking

Preparation of Hybrid Nanofiltration Membranes Based on Schiff Base Reaction for Hard Water Softening

Composite Nanofiltration Membranes Via the Co-Deposition and Cross-Linking of Catechol/Polyethylenimine

Preparation and Performance of Composite Nanofiltration Membrane Modified by Mussel Coating

Nanofiltration Membrane with a Mussel-Inspired Interlayer for Improved Permeation Performance.

A Novel Positively Charged Nanofiltration Membrane Prepared from N,N-dimethylaminoethyl Methacrylate by Quaternization Cross-Linking

Bio-inspired Fabrication of Anti-fouling and Stability of Nanofiltration Membranes with a Poly(dopamine)/Graphene Oxide Interlayer

A Nanofiltration Membrane Preparation Process Based on Polyethyleneimine Diffusion Modulation and Surface Modification

Codeposition of Catechol–polyethyleneimine Followed by Interfacial Polymerization for Nanofiltration Membranes with Enhanced Stability

Nanocomposite Membranes of Polydopamine/electropositive Nanoparticles/polyethyleneimine for Nanofiltration

Nanofiltration membranes with enhanced performance by constructing an interlayer integrated with dextran nanoparticles and polyethyleneimine coating

Nanofiltration‐like forward osmosis membranes on in‐situ mussel‐modified polyvinylidene fluoride porous substrate for efficient salt/dye separation