Enhanced mid-temperature thermoelectric performance of textured SnSe polycrystals made of solvothermally synthesized powders

Li Yiwen,Li Fu,Dong Jinfeng,Ge Zhenhua,Kang Feiyu,He Jiaqing,Du Hongda,Li Bo,Li Jing-Feng

DOI: https://doi.org/10.1039/c5tc04202j

IF: 6.4

2016-01-01

Journal of Materials Chemistry C

Abstract:This work revealed that the thermoelectric properties of textured SnSe polycrystals, which are made of solvothermally synthesized powders with a preferred orientation grown along the (400) plane, can be enhanced, especially in the range of mid-temperatures. The electrical conductivity for the sintered sample is greatly improved in the whole measured temperature range, attributed to the high carrier concentration and unique mobility change. This results in a large power factor combined with the moderate Seebeck coefficient, especially in the range of 300-650 K, which exceeds 5 mu W cm(-1) K-2 at 423 K and even larger than 6 mu W cm(-1) K-2 at 521 K. Benefiting from the enhanced electrical conductivity and the low total thermal conductivity (<1 W m(-1) K-1 in the range of 300 to 773 K), a higher ZT value than that reported for undoped single crystals was achieved in a relatively wide mid-temperature range, which reached 0.44 at 522 K and 0.5 at 573 K, and then showed weak temperature dependence in the range from 573 to 700 K. Above 700 K, the ZT value increased with temperature and a maximum value of nearly 0.6 was obtained at the maximum measured temperature of 773 K for the SnSe sample without any deliberate doping.