Abstract:Industrial interest in wrought heat-treatable aluminium-lithium (Al–Li) based alloys dates back to around 1919 in Germany. However the exploitation of these alloys has historically been limited by their mechanical property anisotropy and concerns over their localized corrosion resistance and temperature stability. Recently, in the last ten years, alloy and process development has resulted in alloy compositions and thermomechanical treatments that potentially can overcome these issues. To put these developments in perspective we have reviewed the corrosion characteristics of first, second and third generation alloys with an emphasis on localized corrosion (intergranular and exfoliation) and stress corrosion cracking (SCC).Intergranular corrosion susceptibility of Al–Li–Cu and Al–Li–Cu–Mg alloys increases with copper content, and the depth of attack increases with ageing, i.e. UA<PA<OA. For alloys that contain zinc the mode of attack is less truly intergranular and more intra-granular or inter-subgranular in nature. Susceptibility to exfoliation corrosion has a similar temper dependence when assessed by conventional EXCO testing, but not following either exposure to a “real-life” outdoor marine environment or to a less aggressive test such as MASTMAASIS. In these tests there are two regimes of exfoliation susceptibility corresponding to under- and over-aged tempers, and an intermediate regime, including peak-aged tempers, with an improved resistance, i.e., UA>PA<OA.SCC initiation from smooth surfaces is rare for copper-free Al–Li alloys irrespective of temper or whether exposure is under continuous or alternate immersion conditions. For copper-containing alloys, initiation remains difficult for smooth specimens under continuous immersion conditions, but occurs readily under conditions of alternate immersion. It is likely that crack initiation is controlled by an anodic dissolution dominated process, but crack propagation may be controlled by either anodic dissolution or a hydrogen related process.Test results reviewed to date on thin plate samples show that the lower lithium content third generation Al–Li alloys, with suitable zinc and/or silver additions and thermomechanical processing can provide an acceptable resistance to localized corrosion (IGC and Exfoliation) and SCC in near to peak aged tempers. For this conclusion to apply to thicker products (>~30 mm) further analysis of corrosion test results is required.

Revisiting stress-corrosion cracking and hydrogen embrittlement in 7xxx-Al alloys at the near-atomic-scale

Revisiting stress-corrosion cracking and hydrogen embrittlement in 7xxx-Al alloys at the near-atomic-scale

Nanoscale perspective on the stress-corrosion cracking behavior of a peak-aged 7XXX-Al alloy

Crack arrest markings in stress corrosion cracking of 7xxx aluminium alloys: insights into active hydrogen embrittlement mechanisms

Enhancing Stress Corrosion Cracking Resistance of Low Cu-Containing Al-Zn-Mg-Cu Alloys by Aging Treatment Control

Hydrogen-accelerated spontaneous microcracking in high-strength aluminium alloys

Hydrogen trapping and embrittlement in high-strength Al-alloys

Hydrogen trapping and embrittlement in high-strength Al alloys

Hydrogen embrittlement revealed via novel in situ fracture experiments using notched micro-cantilever specimens

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile

Inhibiting weld cracking in high-strength aluminium alloys

Effect of extrusion process on the stress corrosion cracking resistance of 7N01 aluminum alloy

Microstructure Imaging, Precipitation Formation and Mechanical Properties: Al–Li and Al–Mg–Zn Alloys

Hydrogen-associated decohesion and localized plasticity in a high-Mn and high-Al two-phase lightweight steel

On the Competition between Intergranular and Transgranular Failure within 7xxx Al Alloys with Tailored Microstructures

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Hydrogen embrittlement of a precipitation-strengthened high-entropy alloy

Quantitative study of the corrosion evolution and stress corrosion cracking of high strength aluminum alloys in solution and thin electrolyte layer containing Cl-

Tailoring negative pressure by crystal defects: Crack induced hydride formation in Al alloys

Study on mechanical properties and hydrogen embrittlement susceptibility of 7075 aluminium alloy

Corrosion and Stress Corrosion of Aluminum–Lithium Alloys