Ca1−xLixAl1−xSi1+xN3:Eu2+ Solid Solutions As Broadband, Color-Tunable and Thermally Robust Red Phosphors for Superior Color Rendition White Light-Emitting Diodes

Le Wang,Rong-Jun Xie,Yuanqiang Li,Xiaojun Wang,Chong-Geng Ma,Dong Luo,Takashi Takeda,Yi-Ting Tsai,Ru-Shi Liu,Naoto Hirosaki

DOI: https://doi.org/10.1038/lsa.2016.155

2016-01-01

Light Science & Applications

Abstract:Color rendition, luminous efficacy and reliability are three key technical parameters for white light-emitting diodes (wLEDs) that are dominantly determined by down-conversion phosphors. However, there is usually an inevitable trade-off between color rendition and luminescence efficacy because the spectrum of red phosphor (that is, spectral broadness and position) cannot satisfy them simultaneously. In this work, we report a very promising red phosphor that can minimize the aforementioned trade-off via structure and band-gap engineering, achieved by introducing isostructural LiSi2N3 into CaAlSiN3:Eu2+. The solid solution phosphors show both substantial spectra broadening (88 -> 117 nm) and blueshift (652 -> 642 nm), along with a significant improvement in thermal quenching (only a 6% reduction at 150 degrees C), which are strongly associated with electronic and crystal structure evolutions. The broadband and robust red phosphor thus enables fabrication of super-high color rendering wLEDs (Ra = 95 and R9 = 96) concurrently with the maintenance of a high-luminous efficacy (101 lm W-1), validating its superiority in high-performance solid state lightings over currently used red phosphors.