MOF Structure Engineering to Synthesize CoNC Catalyst with Richer Accessible Active Sites for Enhanced Oxygen Reduction
Jiaojiao Gao,Yixuan Hu,Yu Wang,Xiaorong Lin,Kailong Hu,Xi Lin,Guoqiang Xie,Xingjun Liu,Kolan Madhav Reddy,Qunhui Yuan,Hua‐Jun Qiu
DOI: https://doi.org/10.1002/smll.202104684
IF: 13.3
2021-11-05
Small
Abstract:Single-atom cobalt-based CoNC are promising low-cost electrocatalysts for oxygen reduction reaction (ORR). However, further increasing the single cobalt-based active sites and the ORR activity remain a major challenge. Herein, an acetate (OAc) assisted metal-organic framework (MOF) structure-engineering strategy is developed to synthesize hierarchical accordion-like MOF with higher loading amount and better spatial isolation of Co and much higher yield when compared with widely reported polyhedron MOF. After pyrolysis, the accordion-structured CoNC (CoNC (A)) is loaded with denser CoN<sub>4</sub> active sites (Co: 2.88 wt%), approximately twice that of Co in the CoNC reported. The presence of OAc in MOF also induces the generation of big pores (5-50 nm) for improving the accessibility of active sites and mass transfer during catalytic reactions. Consequently, the CoNC (A) catalyst shows an admirable ORR activity with a E<sub>1/2</sub> of 0.89 V (40 mV better than Pt/C) in alkaline electrolytes, outstanding durability, and absolute tolerance to methanol in both alkaline and acidic media. The CoNC-based Zn-air battery exhibits a high specific capacity (976 mAh g<sup>-1</sup> <sub>Zn</sub> ), power density (158 mW cm<sup>-2</sup> ), rate capability, and long-term stability. This work demonstrates a reliable approach to construct single atom doped carbon catalysts with denser accessible active sites through MOF structure engineering.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology