Scalable Seashell-Based CVD Growth of 3 D Graphene Foams for Oil-Water Separation
Liurong Shi,Ke Chen,Ran Du,Alicja Bachmatiuk,Mark Hermann Rümmeli,Kongwei Xie,Youyuan Huang,Yanfeng Zhang,Zhongfan Liu
2016-01-01
Abstract:A seashell-based CVD technique for preparing 3D graphene foams is reported. The graphene sheets in thus-obtained foams are seamlessly interconnected into a three-dimensional flexible network, forming highly porous materials with negligible noncarbon impurities, ultralow density, outstanding mechanical flexibility and electrical conductivity. These 3D graphene foams demonstrated a fast adsorption performance towards various oils and organic solvents with adsorption capacity up to 250-fold weight gain. The present approach offers a practical route for scalable constructing 3D graphene foams for versatile applications such as energy storage and water remediation. Three-dimensional (3D) graphene foam, a combination of twodimensional (2D) graphene building blocks and 3D porous structures, has attracted significant attention in recent years . Such kinds of graphene foams are self-supporting materials, possessing the fascinating intrinsic properties of graphene together with high porosity and ultralow density. A number of approaches such as sol-gel process and template growth have been reported for fabricating 3D graphene foams . Sol-gel process of graphene oxide usually creates materials with abundant structural defects, chemical impurities, and discontinuous interconnections between individual graphene sheets arising from the solution process. Therefore, seriously degradation of the intrinsic properties of graphene such as electron and phonon transports, will appear. Templateassisted chemical vapor deposition (CVD) provides an effective way to synthesize 3D graphene foams composed of seamless interconnected graphene sheets with high purity and quality . For instance, graphene foams grown from nickel foam template have demonstrated excellent mechanical strength and superior electrical conductivity [1, 7, . However, intrinsic drawbacks exist in this approach, including the time-consuming template-removing process, the unavoidable metal residues, and the limited choice of metal foams and their microstructures. For practical applications, cost issue should also be taken into account. Obviously, mass production of 3D graphene foams would consume great amounts of expensive nickel metals. It is extremely attractive to develop low cost and easily removable CVD growth templates for industrial fabrication of 3D graphene foams. In this light, we turn our attention to the natural seashells. Seashells are the shells of oceanic mollusks with great abundance. The main chemical composition of seashells is calcium carbonate . Depending on the source mollusks, seashells have versatile microscopic structures. Furthermore, a simple chemical calcination can easily convert the biological calcium carbonate into calcium oxide without destroying the structural framework, which can then be readily washed away by dilute acid. In this work, we demonstrate the CVD template function of seashells for fabricating 3D graphene foams for the first time. Scallop was employed as the typical example for demonstration, which has massive worldwide production . In this way, graphene foams with high purity, high porosity, ultralow density and superior bendability have been synthesized. More interesting, bespoke shape control of such graphene foams can be easily achieved through lime slaking process of calcium oxide. Notably, the present approach was also extended to other seashells, offering the great opportunities in controlling the microscopic structures of graphene foams. In virtue of their unique structures and properties, the applications of obtained graphene foams as binderfree Li-ion battery anodes and oil adsorbents have been demonstrated. Figure 1. Fabrication process of scallop-derived 3D graphene foams. a) Schematic illustration of graphene foam formation. b) SEM image of pristine scallop microstructure. c) SEM image of calcined scallop at 1050 °C for 30 min in air. d) Graphene coated calcined scallop after CVD growth at 1020 °C for 30 min. e) 3D Page 1 of 5 ACS Paragon Plus Environment Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 graphene foam after removing the CaO framework. Insets of b), c), d) and e) are the corresponding photographs. All the scale bars are 5 μm. The fabrication procedure of 3D graphene foam using scallop template is schemed in Figure 1a. Scallop, a naturally abundant biomass, is composed of calcium carbonate (95 vol%) and organic biopolymers (5 vol%) . Inside the scallop, the architecture resembles a three-dimensional brick and mortar wall at the mesoscale level [11] (Figure 1b). However, the tight packing of the calcium carbonate is not suitable for directly CVD growing graphene foams since carbon species cannot effectively enter into the pores which is required for graphene growth. When heated in air, the organic molecules and CaCO3 in scallop start to decompose along with releasing CO2 gas. This leads to an interconnected porous structure within the scallop bulk while keeping the scallop framework unchanged (Figure 1c). At the same time, CaCO3 inside the scallop shell fully converts to CaO following the reaction below [12] (Figure S1):