Abstract:Bare growth defects are well known to be widely spread inside zeolite crystals. However, still no reports have been published to date on how to engineer the defects inside zeolite crystals for fabricating mesoporous zeolite single crystal. Very recently, Mintova and co-workers reported on capturing ultrasmall EMT zeolite from template-free systems by heating silica gel gently for a short time only. High temperature or long syntheses transformed the EMT structure of the first metastable crystalline product into more stable cubic faujasite and denser sodalite. It has been possible to catch the metastable phases at the very early stages of crystallization in colloidal systems during zeolite synthesis. This significant achievement opened the door to the synthesis of complicated nanostructure of zeolites through a simple, efficient and green strategy, and has also encouraged us to study the early stages of zeolite crystallization with a view to engineering the growth defects. In the current work, tender crystallization conditions (crystallization temperature of 100 °C, high concentration of TPAOH) and an ap-propriate original Si/Al ratio of 198 have been adopted to control the nucleation-growth rate, and therefore, successfully monitor the early stages of ZSM-5 zeolite crystallization. After crystallizing the clear sol with a molar composition of 25SiO2: 0.0625Al2O3: 0.1Na2O: 11TPAOH: 426.5H2O: 100EtOH for 10 d at 100 °C, we obtained the hierarchical ZSM-5 zeolite colloid nanocrystals (HCN-ZSM-5) with abundant uniform intracrystalline mesopores. These mesopores were further proved to be derived from the decomposition of adjacent several layers microporous channels, as the growth defects, leading to highly uniform small mesopores of 2.2 nm diameter, were distributed in every nanosized crystal. Moreover, this HCN-ZSM-5 showed high crystallinity yields of 60%-90%, high crystallinity, good hydrothermal stability and high surface area. The formation of HCNZSM-5 underwent two processes, viz. oriented-aggregation growth and growth-dissolution-regrowth. It was observed that the original Si/Al ratio directly regulated the formation of HCN-ZSM-5, and then the crystallization tempera-ture and the concentration of TPAOH influenced the particle diameter, crystalline yield and BET surface area.

On the Mesoporogen-Free Synthesis of Single-Crystalline Hierarchically Structured Zsm-5 Zeolites in A Quasi-Solid-State System

Mesoporogen-Free Synthesis of Hierarchically Structured Zeolites with Variable Si/Al Ratios via a Steam-Assisted Crystallization Process

Efficient Synthesis of Mesoporous Nano ZSM-5 Zeolite Crystals without a Mesoscale Template

One-pot Synthesis of Hierarchically Structured ZSM-5 Zeolites Using Single Micropore-Template

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Synthesis of ZSM-5 with Hierarchical Porosity: In-situ Conversion of the Mesoporous Silica-Alumina Species to Hierarchical Zeolite

Green Routes for the Synthesis of Hierarchical HZSM-5 Zeolites with Low SiO2/Al2O3 Ratios for Enhanced Catalytic Performance

Synthesis of Mesoporous Zeolite Single Crystals with Cheap Porogens

Synthesis of hierarchically porous ZSM-5 zeolites by steam-assisted crystallization of dry gels silanized with short-chain organosilanes

High-Surface-Area Zeolitic Silica with Mesoporosity

Highly Stable Hierarchical ZSM-5 Zeolite with Intra- and Inter-Crystalline Porous Structures

Mesoporogen-Free Synthesis of High-Silica Hierarchically Structured ZSM-5 Zeolites and Their Superior Performance for the Methanol-to-Propylene Reaction

Facile Synthesis of Mesoporous Aluminosilicates Constructed with Crystalline Microporous Frameworks

Sustainable Synthesis of Hierarchically Porous Silicalite-1 Zeolite by Steam-assisted Crystallization of Solid Raw Materials Without Secondary Templates

Organic-Free Synthesis of Hierarchical ZSM-5 Via a Combined Strategy of Unstable Precursors and Postsynthesis Steam Treatment

Sub-micron sized hierarchical porous ZSM-5 particles with controllable mesoporous structures by changing the alkalinity in the synthesis using NaOH

Facile Synthesis of Mesostructured ZSM-5 Zeolite with Enhanced Mass Transport and Catalytic Performances

Hydrophilicity/hydrophobicity Modulated Synthesis of Nano-Crystalline and Hierarchically Structured TS-1 Zeolites

ZSM-5 Zeolite Colloid Nanocrystal with Intracrystalline Mesopores from Growth Defects

Facile synthesis of ZSM-5 mesocrystal via novel pathway of crystallization: Fast precipitation, deconstruction and reorganization

Direct Synthesis of Monolithic Nano-Sized ZSM-5 Aggregates Possessing Ordered Mesoporosity by Controlling Arrangement of Nanoparticles