Electrostatic Interaction-Controlled Formation of Pickering Emulsion for Continuous Flow Catalysis

Fangjun Peng,Jie Xu,Haolan Xu,Haifeng Bao

DOI: https://doi.org/10.1021/acsami.0c17857

2020-12-29

Abstract:Although noble metal or non-noble metal-catalyzed reactions are widely used, it is still difficult to apply these reactions in the large-scale synthesis of chemicals because most of the reactions are carried out by the inefficient batch reaction strategy. Herein, Pickering emulsion-based continuous flow catalysis was utilized to address this problem. Cellulose nanofibers with aldehyde groups (ACNF) were generated through oxidizing C2 and C3 hydroxyl groups of cellulose nanofibers into aldehyde groups by NaIO₄, followed by <i>in situ</i> depositing Ag nanoparticles on ACNF to produce Ag-decorated ACNF () via a facile aldehyde-induced reduction method. with ∼2 wt % Ag () has been used to prepare the Pickering emulsion by controlling the electrostatic interaction between and the oil–water interface via adjusting the pH. It was found that the Pickering emulsion could be generated at a pH around 3.29 and was determined to be the oil-in-water emulsion. The reduction of organic molecules (4-nitrophenol (4-NP), methylene blue (MB), and methyl orange (MO)) was selected as a model reaction to test the reliability of the Pickering emulsion in continuous flow catalysis, which demonstrated very high conversion rates for 4-NP (&gt;98%, 50 h), MB (&gt;99%, 30 h), and MO (&gt;96%, 40 h).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17857?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17857</a>.TEM image of (Figure S1); TEM images of and (Figure S2); SEM images of solidified Pickering droplets (Figure S3); pictures of the aqueous suspension (Figure S4); pictures of the mixture of NaBH4 (0.25 M) and organic substances (Figure S5); pictures of the mixture of the Ag nanoparticle suspension and toluene (Figure S6); continuous flow reactor and UV–vis absorption spectra for the emulsion and suspension (Figure S7); UV–vis absorption spectra of the influent solution and effluent solution for the continuous reduction of 4-NP (Figure S8); LC-MS chromatogram of the reduction products (Figure S9); light microscopy image (Figure S10); and molecular structures (Figure S11) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17857/suppl_file/am0c17857_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology