Abstract:N,O-Carboxymethylchitosan(CMC) beginning with chitosan and chloracetic acid by stepwisely increasing temperature method was synthesized. Carboxymethylation substitutive degree is 1.84, average molecular weight is 3.08x10(5) and instrinsic viscosity (25+/-0.5)degreesC is 180 L/g. It was characterized by ultraviolet spectrum, infrared spectrum, fluorescence spectrum. Its ultraviolet characteristic absorption peak is at 206 nm arising from n-->pi electron transition. However, the ultraviolet characteristic absorption peak of chitosan is at 195 nm. One of stretching vibration absorption peak of CMC infrared spectrum is at 1635 cm(-1) which results from stretching vibration of -C=O(-COOH) bond. But at 1635 cm(-1) there is no stretching vibration peak of C=O in the chitosan infrared spectrum. In fluorescence spectrum, the excitation wavelength of CMC is 330 nm and its emission wavelength is 407 nm. The excitation wavelength of Chitosan is 320 nm and its emission wavelength is 391 nm. Synthesized CMC is soluable in the aqueous solution. It is a macromolecular surface-active agent. CMC surface tension linearly decreases with the increasing of CMC concentration in aqueous solution. But its conductivity linearly increases with the increasing of CMC concentration in the aqueous solution. The CMC aggregate behaviors in CMC aqueous solution is also studied, which shows that there is a some degree aggregation in the aqueous solution of synthesized carboxymethylchitosan. Meanwhile, the Zeta potential of CMC aqueous solution is studied. It demonstrates that Zeta potential value decreases with the decreasing of the concentration of CMC: The study indicates CMC is an amphoteric macromecleular electrolyte and its isoelectronic point is 7.28. Therefore, the pH value and concentration of CMC have great influence on the stability of CMC aqueous solution.

Preparation and Characterization of Carboxymethyl-Functionalized Chitosan Fiber

Potential of quaternization-functionalized chitosan fiber for wound dressing

Preparation and properties of alginate/carboxymethyl chitosan blend fibers

Liquid handling properties of carboxymethyl modified chitosan nonwovens for medical dressings

Preparation of Carboxymethyl Chitosan Sulfate for Improved Cell Proliferation of Skin Fibroblasts

The Evaluation on Biological Properties of Carboxymethyl-Chitosan and Carboxymethyl-Chitin

N-carboxyethyl chitosan fibers prepared as potential use in tissue engineering.

Preparation, Characterization and Antimicrobial Activity of Quaternized Carboxymethyl Chitosan and Application As Pulp-Cap

Synthesis and Studies on Properties of N,O-Carboxymethylchitosan

Preparation and Characterization of Water-Soluble N,O-carboxymethylchitosan

Preparation, Characterization and Feasibility Study of Dialdehyde Carboxymethyl Cellulose As a Novel Crosslinking Reagent.

Preparation and Characterization of Chitosan/Carboxymethyl Cellulose Compound Membrane

A New Approach to Chemically Modified Carboxymethyl Chitosan and Study of Its Moisture‐absorption and Moisture‐retention Abilities

Preparation and characterization of carboxymethylcelluloses and methylcelluloses from abaca, flax, hemp, jute and sisal pulps

Preparation and Structural Characterization of O-Carboxymethyl Chitosan

Synthesis and Characterization of N, O-Carboxymethyl Chitosan

Characteristics of chitosan fiber and their effects towards improvement of antibacterial activity

Preparation and Properties of Viscose Rayon/O-carboxymethyl Chitosan Antibacterial Fibers

Preparation and characterization of carboxymethyl cellulose containing quaternized chitosan for potential drug carrier

Preparation, Characterization and the Effect of Carboxymethylated Chitosan–cellulose Derivatives Hydrogels on Wound Healing

Preparation and Properties of Carboxymethyl Κ-Carrageenan/alginate Blend Fibers