Enhanced High‐Frequency Properties of NiZn Ferrite Ceramic with Co2Z‐Hexaferrite Addition

Zongliang Zheng,Huaiwu Zhang,Qinghui Yang,Lijun Jia
DOI: https://doi.org/10.1111/jace.13003
IF: 4.186
2014-01-01
Journal of the American Ceramic Society
Abstract:Significantly enhanced dielectric and loss characteristics have been observed in Ni0.4Zn0.6Fe2O4 ferrite with various Ba3Co2Fe24O41 (Co2Z) addition (x). Compared with pure NiZn and Co2Z ferrites, the composite ceramics obtain much refined grains and notable high‐frequency characteristics. With the introduction of Co2Z into NiZn ferrite matrix, the resistivity is largely increased from the order of 106 Ω cm to the order of 108 Ω cm and the frequency stability of permittivity is dramatically enhanced. Co2Z addition obviously improves the magnetic quality factor Q and reduces the dielectric loss of the ceramics at high frequency. For the samples with x = 20−30 wt%, permittivity ε′ is almost unchanged from 1 MHz to 1 GHz, Q is greater than 10 in a wide frequency range, and dielectric loss tan δε is observed to be of the order of 10−3 at 100 MHz, which is lower by two orders of magnitude compared with pure NiZn and Co2Z ferrites. These characteristics are all desirable for magneto‐dielectric ferrites in high‐frequency applications.
What problem does this paper attempt to address?