Impact of Ca 2+ and Zr 4+ substitution on mechanical energy harvesting response of lead-free BaTiO 3 piezoceramics with thermally stable storage density and efficiency
Tejas K. Jadhav,Nikita J. Kapadi,Tulshidas C. Darvade,V.R. Reddy,Ajit R. James,Rahul C. Kambale
DOI: https://doi.org/10.1016/j.mtcomm.2024.110521
IF: 3.8
2024-09-30
Materials Today Communications
Abstract:The Ba 1-x Ca x Zr y Ti 1-y O 3 (BCZT; x = 0.18, y = 0.08; x = 0.15, y = 0.10; x = 0.12, y = 0.12; x = 0.09, y = 0.14; both x and y are in mol. %) piezoceramics were prepared by solid-state reaction method and investigated their energy storage and harvesting responses. The composition x = 0.15, y = 0.10 ( i.e. BCZT-2) reveals the morphotropic phase boundary (MPB) near room temperature with enhanced piezoelectric properties such as piezoelectric charge coefficient ( d 33 ) ∼ 380 pC/N , piezoelectric strain coefficient ( d 33 * ) ∼ 583.71 pm/V , piezoelectric voltage coefficient ( g 33 ) ∼ 14.09 ×10 −3 Vm/N , figure of merits ( d 33 ×g 33 ) ∼ 5.35 ×10 −12 m 2 /N and the electromechanical coupling coefficient ( k p ) ∼ 0.291. The harvested peak-to-peak open circuit AC voltage is 30 V and the calculated current is in the range of 0.02–0.14 mA with varied load resistance and the maximum obtained power density is 13.38 μW/mm 3 for BCZT-2 ceramics. The DC output signal of BCZT-2 ceramics successfully lit up the ' FCLNT ' panel consisting of 53 red LEDs. At room temperature, BCZT ceramics have a recoverable energy storage density ( W rec ) and storage efficiency ( η ) in the range between 506.46 and 257.49 m J/cm 3 and 50.53 – 64.93 % respectively. The composition x = 0.12, y = 0.12 (i.e. BCZT-3) revealed the highest energy storage efficiency ( η ) ∼ 64.93 % at room temperature. Nonetheless, the temperature-dependent (till its Curie temperature) maximum obtained W rec of all BCZT ceramics is found in the range between 238.41 and 446.49 m J/cm 3 with an η of 66.98–79.67 %. Thus, compositionally tuned BCZT ceramics exhibit considerable piezoelectric properties, including energy storage and harvesting capabilities.
materials science, multidisciplinary