Thermal Depolarization in the High-Temperature Ternary Piezoelectric System x PbTiO 3 - y BiScO 3 - z Bi(Ni 1/2 Ti 1/2 )O 3

shantao zhang,jurgen rodel,eva sapper,david p cann,troy y ansell

DOI: https://doi.org/10.1111/jace.13268

IF: 4.186

2014-01-01

Journal of the American Ceramic Society

Abstract:In the high-temperature ternary perovskite piezoelectric system xPbTiO(3)-yBiScO(3)-zBi(Ni-1/2,Ti-1/2)O-3 (PT-BS-BNiT), the addition of bismuth to the A site and nickel to the B site leads to compositions that exhibit diffuse relaxor-like behavior. For these, depolarization temperature, not Curie point, is the critical value of temperature. Depolarization temperature (T-d) is defined as the temperature at which the steepest loss in polarization occurs. This temperature is observed in poled materials through two different methods: loss tangent measurements and in situ d(33). Across the ternary system, multiple dielectric anomalies occurred which was observed in dielectric tests where the dielectric peak broadens and becomes frequency dependent as BNiT content increased. For different compositions, the value of T-d ranged between 275 degrees C-375 degrees C. Values for the piezoelectric coefficient increased with temperature up to d(33)=1000pC/N during in situ d(33). High temperature (up to 190 degrees C) and high field (up to 40kV/cm) were also applied to test ferroelectric properties in these regimes.