New Antiferroelectric Solid Solution of Pb(Mg1/2W1/2)O3–Pb(Zn1/2W1/2)O3 As Dielectric Ceramics

Zihe Ren,Nan Zhang,Xifa Long,Zuo-Guang Ye

DOI: https://doi.org/10.1111/jace.12966

IF: 4.186

2014-01-01

Journal of the American Ceramic Society

Abstract:A new solid solution of (1−x)Pb(Mg1/2W1/2)O3–xPb(Zn1/2W1/2)O3 has been prepared in the form of ceramics by solid‐state reaction with composition x up to 30%. It is found that with the substitution of Zn2+ for Mg2+ on the B site of the of complex perovskite structure the antiferroelectric (AFE) Curie temperature TC of PMW increases from 40°C (x = 0) to 67°C (x = 30%), indicating an enhancement of antiferroelectric order, whereas, at the same time, the phase transition becomes more diffuse due to a higher degree of chemical inhomogeneity. X‐ray diffraction analysis indicates that the crystal structure adopts an orthorhombic space group (Pmcn) with a decrease in lattice parameter a, but an increase in b and c as the Zn2+ concentration increases. The low dielectric constant (~ 102), low dielectric loss (tanδ ≈ 10−3), linear‐field‐induced polarization, and significantly high breakdown field (~ 125 kV/cm) at room temperature make this family of dielectric materials a promising candidate for ceramic insulators.