Biodiesel Production with Solid Catalysts
Feng Guo,Zhen Fang
DOI: https://doi.org/10.5772/25602
2011-01-01
Abstract:from the products, water-washing process and neutralization steps were avoided.Contaminated water from this process was greatly reduced, and the sewage treatment fees were also minimized.New types of heterogeneous catalysts have mushroomed and developed in recent years. Heterogeneous acid catalystsAcid catalysts can simultaneously catalyze both esterification and transesterification, showing a much higher tolerance to FFAs and water than basic homogeneous catalysts (e.g., www.intechopen.comBiodiesel -Feedstocks and Processing Technologies 340 NaOH and KOH).Homogeneous acid-catalyzed reaction is about 4000 times slower than the homogeneous base-catalyzed reaction (Lotero et al., 2005).Heterogeneous acid catalysts performed less activety, but they are favorable for low-qualified oil feedstocks with high FFAs.Now, synthetic solid acids have already amounted to hundreds of species, most of them can be used in esterification and transesterification reactions.Solid acids keep stable activity in conversion of low-qualified oils or fats to biodiesel.Currently developed solid acid catalysts are introduced in the following sections: cation exchange resin (i.e.Amberlyst-15 and NR50), mineral salts (i.e.ferric sulfate, zirconium sulfate, alum phosphate and zirconium tungsten), supported solid acid and heteropolyacid catalysts. Ion-exchange resinsIon-exchange resins are widely used in important industrial processes for both separation and reaction applications.They are less expensive than lipase and supercritical methanol.Ion exchange resins also help to separate biodiesel and glycerol.Shibasaki-Kitakawa et al. (2007) found catalytic activity of anion-exchange resins correlated positively with crosslinking degree and particle size.The activity of acid ion-exchange resins for the esterification reaction is influenced by the accessibility of reactants to the matrix anchored sulfuric acid groups located at the surface or inside the resins.Mass-transfer restriction is another factor affecting catalytic activity.Internal diffusion was found to cause mass-transfer restriction and is rate-limiting for regular resins.Most of the active sites are embedded in the gel matrix, so the resins with macro-pores have high catalytic activity.Furthermore, the catalytic activity decreased when the cross-linking degree of polymeric matrix increased.Reusability is an important evaluation index for industrial applications of resins.Mechanical strength and thermo-stability are important for the large-scale applications of resins in biodiesel production.Ion exchange resins usually don't change catalytic property for long time operation at low temperature (< 100 o C).Caetano et al. (2009) studied esterification of palmitic acid with methanol using poly(vinyl alcohol) cross-linked with sulfosuccinic acid (SSA) resin at 60°C, about 90% conversion rate was achieved after 2 h.Only about 5% sulfosuccinc acid was leached after 7 recycles.Activity of NKC-9 resin even slightly increased at the first 10 runs, due to breakdown of resin particles under mechanical agitation (Feng et al., 2010).Continuous production of biodiesel in a fixed-bed reactor packed with resins was successively operated (Shibasaki-Kitakawa et al., 2007;Liu et al., 2009;Feng et al., 2011).After 500 h, conversion yield of FFAs still kept over 98%.Amberlyst-15 performed high activity at 100 o C in the fixed-bed, and a 97.5% FAMEs yield was achieved (Son et al. 2011).Combination of fixed-bed reactor with supercritical CO 2 may develop a continuous process that is preferred for massive biodiesel production.Catalyst deactivation is caused by salt contaminants and water-swelling.Catalytic active sites on acidic resins can exchange with salt ions contained in oil.Traces of Na, K, Mg and Ca lead to a continuous activity loss (Russbueldt and Hoelderich, 2009).Deactivated catalyst can be recovered to its original activity by acid washing.It was found that temperature has negligible effect on water-swelling, but the water absorbed on the resin surface can be extracted by excessive methanol (Tesser et al., 2010).. ZeolitesZeolites are crystalline alumino-silicates with a three-dimensional porous structure.They can be synthesized with different crystal structures, definitive pore sizes, framework Si/Al ratios and adjustable acid centers to have some important catalytic properties.Aluminum