Abstract:The ductility of metallic materials is recognized to be significantly affected by stress state and strain rate. However, systematic investigations on the impacts of stress state and strain rate on ductile behavior are infrequent, and only a minority of fracture models can consider both effects concurrently. This work aims to systematically investigate the ductile response of Ti6Al4V alloy over a broad spectrum of stress states and strain rates and to propose a ductile model that incorporates the coupled influence of stress state and strain rate. First, five types of specimens were employed to obtain distinct stress states. Then, the fracture strain of material was ascertained for strain rate spanning from 10 −3 /s to 10 3 /s, stress triaxiality ranging from -0.7 to 0.4, and Lode angle parameter varying from -1 to 1 using a combined experimental-numerical method. It was found that over a broad spectrum of stress states, the relation between fracture strain versus stress state is not monotonic, and the fracture strain reduces as strain rate increases. Utilizing the experimental data, a novel ductile fracture model incorporating the stress triaxiality, Lode angle parameter and strain rate was established and embedded into the ABAQUS/Explicit through the user material subroutine VUMAT. Finally, a validation test was conducted to demonstrate the validity of the proposed model. The results indicate the satisfactory correlation between experiment and calculation for fracture displacement and fracture morphology, which illustrates that the proposed model can predict the ductile behavior across a wide spectrum of stress states and strain rates. This work provides a definite theoretical guidance for the optimization design and safety evaluation of Ti-6Al-4V alloy structural components.

Mechanism-Based Numerical Approach to Ductile Fracture in an 2024–T3 Aluminium Alloy

Tensile and shear failure mechanisms of 2024-T3 aluminum alloy

Experimental and numerical investigations into the ductile fracture during the forming of flat-rolled 5083-O aluminum alloy sheet

Effect of stress triaxiality and normalized Lode angle on ductile fracture of aluminum 2139-T8

An uncoupled ductile fracture model considering void shape change and necking coalescence

Plasticity and ductile fracture modeling of an Al–Si–Mg die-cast alloy

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

Damage and fracture initiation under shear and compression stress states in the aluminum alloy EN AW6082-T6

A damage sequence interaction model for predicting the mechanical property of in-service aluminium alloy 6005A-T6

Analysis of Ductile Fracture by Extended Unified Strength Theory

Experimental and numerical investigation on plasticity and fracture behaviors of aluminum alloy 6061-T6 extrusions

Fracture Prediction of Aluminum Alloy Sheet AA2024-T3 Using Analytical Stress and Experimental Strain Based Failure Criteria

Modeling of the Ductile Fracture During the Sheet Forming of Aluminum Alloy Considering Non-Associated Constitutive Characteristic

Characterization and prediction of fracture in 6000- and 7000-series aluminum alloy sheet under various stress states

Ductile Failure Predictions for the Three-Point Bending Test of a Complex Geometry Made From Aluminum Alloy

Coupled effect of stress state and strain rate on ductile fracture of Ti6Al4V alloy

Analysis of ductile damage and fracture under reverse loading

A user-friendly anisotropic ductile fracture criterion for sheet metal under proportional loading

Numerical Analysis of Experiments on Damage and Fracture Behavior of Differently Preloaded Aluminum Alloy Specimens

Experimental and Numerical Study on Shear-Punch Test of 6060 T6 Extruded Aluminum Profile

Fracture prediction for metal sheet deformation under different stress states with uncoupled ductile fracture criteria