Preparation and Properties Investigation on a Kind of Pseudopolyrotaxane Hydrogel with High Intensity
Xiao-zhen Li,Si-chao Tian,Peng-fei Sun,Qu-li Fan,Wei Huang
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16311
2017-01-01
Acta Polymerica Sinica
Abstract:As an important member of supramolecular hydrogel, pseudopolyrotaxane (PPR) hydrogel has attracted tremendous attention in recent years due to its good biocompatibility. Compared with conventional approaches reported, a new method was developed for PPR hydrogel preparation in this study, which can increase the strength of the hydrogel more efficiently. First, monoaccharide group-functionalized methoxypolyethylene glycols (MPEG) (MPEG-Glc, MPEG-Man and MPEG-Gal) were synthesized by click chemistry. After that, a series of PPR hydrogels (Glc-PPR, Man-PPR and Gal-PPR) with high stability and strength were successfully prepared via the "host-guest" interactions between alpha-CD and monoaccharide group-functionalized MPEG (MPEG-Glc, MPEG-Man and MPEG-Gal, respectively). However, similar hydrogel cannot be obtained using alpha-CD and MPEG without monoaccharide modification. The properties of Glc-PPR, Man-PPR and Gal-PPR were characterized by rheometer test, X-ray diffraction (XRD) and scan electron microscopy (SEM). Surprisingly, rheometer test results indicated that the elasticity modulus of Glc-PPR, Man-PPR and Gal-PPR could be up to 1.0 x 10(5) Pa, which was much higher than that of the clay-enhanced hydrogel in the previous reports. As for this phenomenon, we propose that new sugar cross-linking agents from "carbohydrate-carbohydate interaction" have constructed among monoaccharide terminals of MPEG, so that the strength of Glc-PPR, Man-PPR and Gal-PPR could be improved efficiently. Furthermore, in order to demonstrate the mechanism of the strength enhancement of PPR hydrogel, phenylboronic acid cyclic monoester (PNIPAM-co-PBOB) and concanavalin A (Con A) were added into Glc-PPR, Man-PPR and Gal-PPR, respectively to eliminate the sugar cross-linking agents, which led to a significant decrease in the strength of Glc-PPR, Man-PPR and Gal-PPR. SEM and XRD results showed that the microstructures of Glc-PPR, Man-PPR and Gal-PPR were basically identical with PPR hydrogel reported in the references, which further confirmed that the PPR hydrogel was prepared successfully. Given its many merits of high intensity, non-toxicity and excellent biocompatibility of the obtained PPR hydrogel, it is expected that the PPR as prepared here will play an important role in drug delivery and biomedical engineering.