Photoluminescence and magnetic properties of Fe-doped ZnS nano-particles synthesized by chemical co-precipitation
Nie Eryong,Liu Donglai,Zhang Yunsen,Bai Xue,Yi Liang,Jin Yong,Jiao Zhifeng,Sun Xiaosong
DOI: https://doi.org/10.1016/j.apsusc.2011.03.114
IF: 6.7
2011-01-01
Applied Surface Science
Abstract:This paper is focusing on the synthesis of Zn 1-xFe xS nano-particles with x = 0, 0.1 and 0.2 by chemical co-precipitation method, the prepared of which are characterized by XRD, EDS, TEM, PL, magnetization versus field behavior and M-T curve. In the XRD patterns, Zn 1-xFe xS nano-particles are shown of cubic zinc blende structure, and the broadening diffraction peaks consistent with the small-size characteristic of nano-materials. The diameter of nano-particles is between 3.3 and 5.5 nm according to the HR-TEM images. The EDS data confirm the existence of Fe ions in Fe-doped ZnS nanoparticles. There we found that Fe-doping did not import new energy bands or defect states, but reduced the intensity of PL peaks. The magnetization versus field behaviors were illustrated by the M-H curves at both 5 K and 300 K, respectively, where no remanence or coercive force was observed. This phenomenon indicates that the Zn 1-xFe xS (x = 0.1) nano-particles are superparamagnetic. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization curves further reveal that the blocking temperature (T B) of the superparamagnetic behavior might be below 5 K. © 2011 Elsevier B.V. All rights reserved.