Study on Active Coke‐based Adsorbents for SO2 Removal in Flue Gas

Yanran Zuo,Honghong Yi,Xiaolong Tang,Shunzheng Zhao,Bowen Zhang,Zhixiang Wang,Fengyu Gao

DOI: https://doi.org/10.1002/jctb.4499

IF: 3.709

2015-01-01

Journal of Chemical Technology and Biotechnology

Abstract:BACKGROUNDA series of active coke-based adsorbents from different sources, treated with acid-base, modified by metal compounds and calcined at different temperatures were investigated for SO2 removal from flue gas.RESULTSThe desulfurization performance of the pure active coke was low, but it was improved after treatment with acid-base, especially HNO3. The active coke loaded with 8% Na2CO3 and 7% Cu(NO3)(2) and calcined at 250-350 degrees C was best for SO2 removal. Compared with the untreated active coke, the time for which A-H-8-7 maintained DE at 90% increased from 4min to 40min and the value of DE of A-H-8-7 increased from 0.131mmolg(-1) to 0.526mmolg(-1). The acid-base treatment was effective in forming rich pore structures and HNO3 treatment formed carbonyl groups which favored desulfurization. Sodium and copper modification made a large number of unsaturated groups and chelating bonds formed and sodium and copper elements were dispersed adequately and existed as different compounds in the active coke. The active ingredients for desulfurization were different at different calcination temperatures. Cu(NO3)(2) tended to break down into Cu2O at higher temperatures. Most adsorption products were sulfate species (SO42-) which combined with supported copper and sodium and then formed Na2Cu(SO4)(2).CONCLUSIONActive coke loaded with 8% Na2CO3 and 7% Cu(NO3)(2) and calcined at 250-350 degrees C showed good performance for SO2 removal. (c) 2014 Society of Chemical Industry