Abstract:Heterogeneous nanoparticles are widely used in catalysis, sensors and biology due to their versatile functions. Among the various heterogeneous nanoparticles, Au-Cu2O core-shell nanoparticles show high stability and short response times for use as sensors and catalysts and have thus attracted much attention. Previous studies show that the properties of Au-Cu2O are mainly related to the shape and size of the Au-Cu2O nanoparticles. However, the forming behavior of heterostructures and the mechanism have not been fully explored. In this work, liquid cell transmission electron microscopy (LCTEM) was used to investigate the formation of these interesting Au-Cu2O nanoparticles and their process of aggregation. The electron beam and dispersion of gold nanoparticles are both important parameters for the reduction reaction in in situ LCTEM. The Au-Cu2O core-shell nanoparticles can be synthesized to have two morphologies, multifaceted and cubic. The nanoparticles grew into these different morphologies due to the amount of remaining citrate ligands on the surface of the gold nanoparticles. For the multifaceted nanoparticles, the epitaxy of the two components is confirmed from high-resolution TEM images and electron diffraction patterns with an epitaxial relationship of Au (020)//Cu2O (020) and Au [101]//Cu2O [101]. The growth rate is approximately 210 nm2 s-1. On the other hand, the cubic nanoparticles nucleate and grow independently. The growth kinetics and elemental distributions have been systematically studied. In addition, the nanoclusters would float, rotate, and finally aggregate with the surrounding clusters. This in situ experiment sheds light on the growth mechanisms of nanostructures and will improve the applicability and controllability of heterostructure synthesis.

Influence of Au Nanoparticle Shape on Au@Cu2o Heterostructures

A Mechanistic Study on the Nucleation and Growth of Au on Pd Seeds with a Cubic or Octahedral Shape

Facile synthesis and heteroepitaxial growth mechanism of Au@Cu core–shell bimetallic nanocubes probed by first-principles studies

Preparation,microstructure and formation mechanism of Cu_2O and Au-Cu_2O core-shell nanocube heterostructures

Fabrication of Au–Cu2O core–shell nanocube heterostructures

Selective Growth of Au Nanograins on Specific Positions (tips, Edges and Facets) of Cu2o Octahedrons to Form Cu2o-Au Hierarchical Heterostructures

A Dewetting Route to Grow Heterostructured Nanoparticles Based on Thin Film Heterojunctions

A new strategy for the surface-free-energy-distribution induced selective growth and controlled formation of Cu2O-Au hierarchical heterostructures with a series of morphological evolutions

Morphology-Controlled Synthesis of Hybrid Nanocrystals via a Selenium-Mediated Strategy with Ligand Shielding Effect: The Case of Dual Plasmonic Au–Cu2–xSe

In situ TEM observation of Au-Cu2O core-shell growth in liquids

Au/Cu2O core/shell nanostructures with efficient photoresponses

Synthesis Of 4h/Fcc-Au@Metal Sulfide Core Shell Nanoribbons

Synthesis of Au and Au–CuO Cubic Microcages Via an in Situ Sacrificial Template Approach

In Situ Investigation of Au-Cu2o Core-Shell Nanoparticles Formation by Liquid Cell TEM

Au-Edged CuZnSe2 Heterostructured Nanosheets with Enhanced Electrochemical Performance.

Growth pathways of Cu shells on Au and AuCu seeds: interdiffusion, shape transformations, strained shells and patchy surfaces

Au@Cu Core-Shell Nanocubes with Controllable Sizes in the Range of 20-30 nm for Applications in Catalysis and Plasmonics

Heterostructures: Au-Edged CuZnSe<sub>2</sub>Heterostructured Nanosheets with Enhanced Electrochemical Performance (Small 29/2015)

Epitaxial growth of heterogeneous metal nanocrystals: from gold nano-octahedra to palladium and silver nanocubes.

Synthesis of hybrid Au-Ag2S-Cu2-xS nanocrystals with disparate interfacial features