Structure evolution and electric-field-induced reversible transition in perovskite Na(Nb<sub>1-</sub><i><sub>x</sub></i>Ta<i><sub>x</sub></i>)O<sub>3</sub> ceramics
Ye Tian,Lei Li,Jia Geng,Hongbin Shi,Yonghao Xu,Wenjing Shi,Xu Guo,Liaona She,Li Jin,Wanyin Ge,Xiaoyong Wei
DOI: https://doi.org/10.1111/jace.19226
IF: 4.186
2023-01-01
Journal of the American Ceramic Society
Abstract:Na(Nb1-xTax)O-3 binary solid-solution ceramics with high quality were fabricated by conventional solid-state sintering routes for improving the electric(E)-field-induced irreversible polarization and transition behaviors of NaNbO3. The studied results confirm that this binary solid-solution ceramics exhibit orthorhombic Pbcm space group companying with reduced unit-cell volume at x <= 0.4, and orthorhombic Pbnm space group at x = 0.5. As the Ta5+ content increases in the binary solid-solutions, the E-field-induced irreversible antiferroelectric -> ferroelectric (AFE -> FE) transition becomes reversible at x >= 0.2, giving rise to double-polarization hysteresis; the key E-fields triggering both irreversible and reversible transitions (E-F) increase in general. In particular, the E-field-induced FE phase at x = 0.15 is unstable upon unloading E-field to zero, which can return to AFE phase with time lapse. At x = 0.5, the Curie temperature (T-C) of AFE shifts to below room temperature, but E-field-induced reversible transition is still observed, which results in a nonlinear polarization with the lowest hysteresis and contributes to the largest energy-storage density. This transition is not due to the AFE <-> FE transition but rather to the order <-> disorder behavior of polar clusters or/and nanoregions within nonpolar Pbnm structure matrix.