Abstract:Over the last few decades, polymer concrete (PC) has been finding use in quick repairing of concrete structures. However, there have been only few studies on the mechanical behavior of PC. The aim of this study is to evaluate the mechanical behavior of PC using destructive and non-destructive tests (NDT). The mixtures were prepared with three different polymer ratios (10%, 12%, and 14%) and two different coarse aggregate sizes (4.75–9.5 mm and 9.5–19 mm). The samples were subsequently tested under three different temperatures (−15 °C, +25 °C, and +65 °C). The Taguchi method and analysis of variance (ANOVA) were used to optimize PC mixes based on the compressive, splitting-tensile, and flexural strengths under varying polymer content, coarse aggregate size, and temperature. NDTs, including ultrasonic pulse velocity and electrical resistivity tests, were carried out to gain insights into the porosity and void content of the specimens. Scanning electron microscopy (SEM) was used to analyze the bonding interface between aggregates and polymer, microstructure phase, and pores that were present in the structure of the PC. Results show that a decrease in the temperature from +25 °C to −15 °C led to an improvement in the mechanical properties of PC mixes, whereas an increase in the temperature from +25 °C to +65 °C adversely affected the mechanical properties. Based on NDT, it was found that increasing the coarse aggregate size and polymer ratio reduced the porosity of specimens. This is attributed to the decreased surface area to volume ratio with increasing particle size, which allowed the polymer to completely coat the surface of aggregates. Finally, a set of expressions was proposed to predict the mechanical properties of PC.

Experimental and analytical investigations on the behavior of interface between concrete and polymer cement mortar under hygrothermal conditions

Investigation on Concrete-Pcm Interface under Elevated Temperature: at Material Level and Member Level

Effects of Temperature and Moisture on Concrete-PCM Interface Performance

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

Fracture Mechanisms of Polymer Cement Mortar: Concrete Interfaces

Experimental on the Behavior of Beams Strengthened by Polymer-modified Fiber Cement Mortar Under Hydrothermal Conditions

Research on Properties of High-Performance Cement Mortar for Semiflexible Pavement

Improving bonding performance of PCM-concrete interface under elevated temperatures by using different adhesives

Interactions Between Organic and Inorganic Phases in PA- and PU/PA-Modified-Cement-Based Materials

Fatigue Degradation Properties of Pcm-Concrete Interface

Crack-Spacing-Based Flexural Capacity of Polymer Cement Mortar-Overlay Reinforced Concrete Beams at High Environmental Temperature

The Mechanical Properties of Polymer-cement Mortar

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

Long-Term Performance of External Bonding under Moisture and Temperature Effects

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Optimizing the mixture design of polymer concrete: An experimental investigation

Bond strength evaluation of polymer modified cement mortar incorporated with polypropylene fibers

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Large scale experimental study on bond behavior between polymer modified cement mortar layer and concrete

Molecular Dynamics Study on Mechanical Properties of Interface between Urea-Formaldehyde Resin and Calcium-Silicate-Hydrates

Rheological, mechanical, and abrasion characteristics of polymer-modified cement mortar and concrete