Electrodeposition of Gold Nanoparticle Clusters on Multi-Wall Carbon Nanotubes and the Direct Electrochemistry of Hemoglobin
Zhao Yue,Hong Bo,Fan Louzhen
DOI: https://doi.org/10.6023/a12110877
2013-01-01
Acta Chimica Sinica
Abstract:Three-dimensional structure gold nanoparticle clusters (3D Au) were electrodeposited onto multiwalled carbon nanotubes (MWCNTs) through improved three-step method, which involves: (1) potential cycling (CV, 200 mV.s(-1)) from +1.8 to 0.4 V was performed in 0.5 mol/L K2SO4 solutions for 10 min in order to produce oxide functional groups (carbonyl, hydroxyl, and carboxyl) at the defect sites located at the ends and/or the sidewalls of MWCNTs, (2) electrochemical oxidation of the Au(III) complex to the Au(V) complex from 2 mol/L K2PtCl4+0.1 mol/L K2SO4 aqueous solutions by using potential-step method (PS). The potential was jumped from 0.3 V to 1.1 V with different pulse width and this was repeated until a steady pulse current was reached. and (3) electrochemical transformation of the Au(V) complex to Au nanoparticle clusters on the surface of MWCNTs through cycling from +1.0 to -0.26 V in 0.1 mol/L H2SO4 solutions to the steady state. For comparison, however, experiments were also carried out with CV in the second step (2 mol/L K2PtCl4+0.1 mol/L K2SO4 aqueous solution with 190 cycles: these proved to be the optimal conditions). The morphology of 3D Au/MWCNTs electrode was characterized by transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). The voltammetric behavior of hemoglobin (Hb) on 3D Au/MWCNTs-Nafion has been investigated in 10 nmol/L Hb solution (pH=6 PBS) by cyclic voltammetry (CV) and current-time method (CT). Compared with Au+MWCNTs-Nafion (+means mix together), Au/MWCNTs-Nation (uniform Au nanoparticle dispersion of MWCNTs, which was obtained when the second step adopts cyclic voltammetry instead of potential-step method), 3D Au/MWCNTs-Nafion gave a higher peak current and better reversibility. The higher sensitivity and lower detection limit show that 3D Au/IVIWCNTs-Nafion can offer a conductive microenvironment for the immobilized Hb to achieve direct electrochemistry. The average. coverage (T) of Hb immobilized on 3D Au/MWCNTs-Nafion was calculated to be 7.65 X le mol.cm(-2), testifies a high surface-to-volume ratio. Electron transfer rate constant (k(s)) was calculated to be 1.8 s(-1), which was proved 3D Au/MWCNTs-Nafion is more conducive to direct electron transfer between Hb and the electrode. Hb/Au/MWCNTs-Nafion potential application towards the electrocatalytic reduction of H2O2 was also conducted to show immobilized Hb exhibits excellent biocompatibility and stability. Our work points to a new path for the preparation of 3D Au/MWCNTs nanocomposites, which are promising as electrocatalysts in direct electrochemistry of Hb.